. "Hausnerov\u00E1, Berenika" . "Development in Machining Technology" . . . "978-83-7242-765-6" . . "294"^^ . "8"^^ . "RIV/70883521:28610/14:43871733" . . "Discrepancies in Design Determination of Metal Injection Molded Tensile Test Specimens"@en . . "The paper describes the discrepancies among tensile test specimens for determination of mechanical properties of Metal Injection Molding (MIM) materials. A standard used in Europe - %22Sintered metal materials, excluding hardmetals - Tensile test pieces%22 differs form that proposed by American Metal Powder Industries Federation(MPIF) - %22preparing and Evaluating Metal Injection Molded (MIM) Sintered/Heat Treated Tension Test Speciments%22. While American standard prefers speciments with holes in a T-bone shaped, the European speciments are flat, without holes. Cores in a mold cavity, which form the holes in test pieces are barrier for the flow front, but also the created weld line might be a critical place for powder/binder separation of the feedstock."@en . . "Politechnika Krakowska" . . "P(ED2.1.00/03.0111), P(EE.2.3.20.0104), S" . "28610" . "Discrepancies in Design Determination of Metal Injection Molded Tensile Test Specimens" . . "[0BFC9C1A341D]" . . . "11687" . . "Discrepancies in Design Determination of Metal Injection Molded Tensile Test Specimens"@en . . "2"^^ . . . . "2"^^ . "standard; tensile test; metal injection molding"@en . "Neuveden" . "Huba, Jakub" . "Discrepancies in Design Determination of Metal Injection Molded Tensile Test Specimens" . . . "RIV/70883521:28610/14:43871733!RIV15-MSM-28610___" . "The paper describes the discrepancies among tensile test specimens for determination of mechanical properties of Metal Injection Molding (MIM) materials. A standard used in Europe - %22Sintered metal materials, excluding hardmetals - Tensile test pieces%22 differs form that proposed by American Metal Powder Industries Federation(MPIF) - %22preparing and Evaluating Metal Injection Molded (MIM) Sintered/Heat Treated Tension Test Speciments%22. While American standard prefers speciments with holes in a T-bone shaped, the European speciments are flat, without holes. Cores in a mold cavity, which form the holes in test pieces are barrier for the flow front, but also the created weld line might be a critical place for powder/binder separation of the feedstock." . "Cracow" .