. "This paper deals with problematics of welding of duplex steel with Ni alloy Inconel 622. The GTAW welding procedure was used for the root and SMAW for the main weld. The weldment indicates a tendency to cracking in the SMAW region of weld metal and at a fusion zone during the bend test. Typical chemical composition of Inconel 622 is given in Tab. I. The purpose of experiment was to determine the causes of cracking of weld metal. Light and electron microscopy has been used for a structural analysis of weld which was supplemented by nanohardness measurements. The Charpy impact test was realized on samples from different areas of the weld." . "Anisimov, Evgeniy" . "[56D8711A1C1E]" . "21220" . "Causes of Inconel 622 weld cracking"@en . "RIV/68407700:21220/11:00185055!RIV12-MSM-21220___" . "This paper deals with problematics of welding of duplex steel with Ni alloy Inconel 622. The GTAW welding procedure was used for the root and SMAW for the main weld. The weldment indicates a tendency to cracking in the SMAW region of weld metal and at a fusion zone during the bend test. Typical chemical composition of Inconel 622 is given in Tab. I. The purpose of experiment was to determine the causes of cracking of weld metal. Light and electron microscopy has been used for a structural analysis of weld which was supplemented by nanohardness measurements. The Charpy impact test was realized on samples from different areas of the weld."@en . "Olomouc" . "189320" . "Olomouc" . . . . . . "Univerzita Palack\u00E9ho v Olomouci" . . . "Local Mechanical Properties 2011" . . "2011-11-09+01:00"^^ . . . . "4"^^ . "Rybn\u00ED\u010Dek, Jan" . . "S" . "Causes of Inconel 622 weld cracking"@en . "RIV/68407700:21220/11:00185055" . . . . "978-80-244-2889-5" . "4"^^ . "Anisimov, Evgeniy" . . . "H\u00E1jkov\u00E1, Pavl\u00EDna" . "Horn\u00EDk, Jakub" . . "1"^^ . . "inconel; weld; fractography; nanohardness; impact test"@en . "Causes of Inconel 622 weld cracking" . "Causes of Inconel 622 weld cracking" .