"Vliv koroze pod nap\u011Bt\u00EDm na bezpe\u010Dnost provozu plynovodu - 1. \u010D\u00E1st" . "Plyn : odborn\u00FD m\u011Bs\u00ED\u010Dn\u00EDk pro plyn\u00E1renstv\u00ED" . . "2"^^ . "Vliv koroze pod nap\u011Bt\u00EDm na bezpe\u010Dnost provozu plynovodu - 1. \u010D\u00E1st"@cs . "2"^^ . . . . "Gajdo\u0161, Lubom\u00EDr" . . . "Vliv koroze pod nap\u011Bt\u00EDm na bezpe\u010Dnost provozu plynovodu - 1. \u010D\u00E1st"@cs . "The research conducted by ITAM scientists has indicated that the type of the crack is also important for determining fracture toughness. If the crack is due to stress corrosion, the material\u00B4s resistance to fracture is much weaker than in tha case of fatigue cracks."@en . . "RIV/68378297:_____/09:00328163" . . "89" . . "Influence of SCC on Gas Pipeline Safety - Part One"@en . "stress corrosion cracking; fracture toughness; pipeline"@en . . "P(FT-TA5/076), Z(AV0Z20710524)" . "\u0160perl, Martin" . "7-8" . "5"^^ . "349305" . "Vliv koroze pod nap\u011Bt\u00EDm na bezpe\u010Dnost provozu plynovodu - 1. \u010D\u00E1st" . "CZ - \u010Cesk\u00E1 republika" . . "0032-1761" . "RIV/68378297:_____/09:00328163!RIV10-AV0-68378297" . . "\u010Cl\u00E1nek se zab\u00FDv\u00E1 srovn\u00E1n\u00EDm lomov\u00E9 hou\u017Eevnatosti \u00FAnavov\u00FDch trhlin a trhlin korozn\u011B-nap\u011B\u0165ov\u00E9ho charakteru. V\u00FDsledky ukazuj\u00ED na v\u00FDrazn\u00E9 sn\u00ED\u017Een\u00ED lomov\u00E9 hou\u017Eevnatosti zji\u0161t\u011Bn\u00E9 na vzorc\u00EDch s vygenerovan\u00FDmi korozn\u011B-nap\u011B\u0165ov\u00FDmi trhlinami."@cs . "[34717CFB39FF]" . . . . . "Influence of SCC on Gas Pipeline Safety - Part One"@en . . "\u010Cl\u00E1nek se zab\u00FDv\u00E1 srovn\u00E1n\u00EDm lomov\u00E9 hou\u017Eevnatosti \u00FAnavov\u00FDch trhlin a trhlin korozn\u011B-nap\u011B\u0165ov\u00E9ho charakteru. V\u00FDsledky ukazuj\u00ED na v\u00FDrazn\u00E9 sn\u00ED\u017Een\u00ED lomov\u00E9 hou\u017Eevnatosti zji\u0161t\u011Bn\u00E9 na vzorc\u00EDch s vygenerovan\u00FDmi korozn\u011B-nap\u011B\u0165ov\u00FDmi trhlinami." . .