. . "Hromadka, M." . "CH - \u0160v\u00FDcarsk\u00E1 konfederace" . . . "Jul" . "The article reports on the dependency of friction and wear of a-(Ti,C,N) films on the nitrogen content. The amount of nitrogen N in the film was controlled by partial pressure of nitrogen p(N2) in the Ar + N(2) sputtering gas mixture. It is shown that the incorporation of N in the film results in the increase of (i) the coefficient of friction mu (increases from 0.12 to 0.37), (ii) the coefficient of wear k (increases from 0.16 x 10(-6) to 0.93 x 10(-6) mm(3)/N m) and the decrease of (i) the film hardness H, (ii) effective Young's modulus E*, (iii) the elastic recovery W(e) of film and (iv) the ratio H/E*. The changes of mu and k of the a-(Ti,C,N) film correlate well with changes of the film mechanical properties (H and E*) and its mechanical behavior (W(e), H/E* and the ratio H(3)/E*(2)) characterizing the film resistance to plastic deformation" . . . "000293258600018" . "10.1016/j.surfcoat.2010.12.048" . "Surface and Coatings Technology" . "P(OC10045), Z(AV0Z10100522), Z(MSM4977751302)" . . . . . "RIV/68378271:_____/11:00437339!RIV15-AV0-68378271" . . "0257-8972" . . "Effect of nitrogen on tribological properties of amorphous carbon films alloyed with titanium"@en . "[9CE673781C39]" . . . "Ti(N,C)/a-C films; mechanical properties; friction; wear; reactive magnetron sputtering"@en . . "Effect of nitrogen on tribological properties of amorphous carbon films alloyed with titanium"@en . "Effect of nitrogen on tribological properties of amorphous carbon films alloyed with titanium" . . "RIV/68378271:_____/11:00437339" . "The article reports on the dependency of friction and wear of a-(Ti,C,N) films on the nitrogen content. The amount of nitrogen N in the film was controlled by partial pressure of nitrogen p(N2) in the Ar + N(2) sputtering gas mixture. It is shown that the incorporation of N in the film results in the increase of (i) the coefficient of friction mu (increases from 0.12 to 0.37), (ii) the coefficient of wear k (increases from 0.16 x 10(-6) to 0.93 x 10(-6) mm(3)/N m) and the decrease of (i) the film hardness H, (ii) effective Young's modulus E*, (iii) the elastic recovery W(e) of film and (iv) the ratio H/E*. The changes of mu and k of the a-(Ti,C,N) film correlate well with changes of the film mechanical properties (H and E*) and its mechanical behavior (W(e), H/E* and the ratio H(3)/E*(2)) characterizing the film resistance to plastic deformation"@en . "Effect of nitrogen on tribological properties of amorphous carbon films alloyed with titanium" . "5"^^ . "3"^^ . . "Nov\u00E1k, P." . . . . "205" . "Musil, Jind\u0159ich" . . "196379" . "1"^^ .