. "[89554D840A8D]" . "Pol\u00E1k, Jaroslav" . "Petrenec, Martin" . . . . . "RIV/68081723:_____/08:00317723" . "4"^^ . . "Cylindrical specimens of cast polycrystalline nickel base superalloy Inconel 738LC were cyclically strained under total strain control at 23 and 800 \u00B0C to fracture. Cyclic hardening/softening curves, cyclic stress-strain curves, and fatigue life curves were obtained at both temperatures. Surface relief was studied in specimens fatigued to failure using scanning electron microscopy."@en . "000262126000146" . "P(1QS200410502), P(GA106/07/1507), P(GA106/08/1631), Z(AV0Z20410507)" . "Low cycle fatigue; Inconel 738LC; fatigue life curve"@en . "1013-9826" . "Low cycle fatigue of cast superalloy Inconel 738LC at high temperature"@en . "RIV/68081723:_____/08:00317723!RIV09-AV0-68081723" . . . "Obrtl\u00EDk, Karel" . . . "Low cycle fatigue of cast superalloy Inconel 738LC at high temperature" . "-" . "377201" . . "Chlupov\u00E1, Alice" . "N\u00EDzkocyklov\u00E1 \u00FAnava lit\u00E9 superslitiny Inconel 738LC p\u0159i vysok\u00E9 teplot\u011B"@cs . . "Low cycle fatigue of cast superalloy Inconel 738LC at high temperature"@en . . . "Key Engineering Materials" . . . "CH - \u0160v\u00FDcarsk\u00E1 konfederace" . "4"^^ . "4"^^ . . "Low cycle fatigue of cast superalloy Inconel 738LC at high temperature" . "Cylindrical specimens of cast polycrystalline nickel base superalloy Inconel 738LC were cyclically strained under total strain control at 23 and 800 \u00B0C to fracture. Cyclic hardening/softening curves, cyclic stress-strain curves, and fatigue life curves were obtained at both temperatures. Surface relief was studied in specimens fatigued to failure using scanning electron microscopy." . . "385-387" . . "V\u00E1lcov\u00E9 vzorky lit\u00E9 polykrystalick\u00E9 superslitiny Inconel 738LC byly cyklicky zat\u011B\u017Eov\u00E1ny do lomu v re\u017Eimu \u0159\u00EDzen\u00E9 deformace p\u0159i teplot\u011B 23 \u00B0C a 800 \u00B0C. Byly stanoveny k\u0159ivky cyklick\u00E9ho zpevn\u011Bn\u00ED/zm\u011Bk\u010Den\u00ED, cyklick\u00E9 deforma\u010Dn\u00ED k\u0159ivky a k\u0159ivky \u017Eivotnosti p\u0159i obou teplot\u00E1ch. Povrchov\u00FD reli\u00E9f byl studov\u00E1n s pou\u017Eit\u00EDm SEM na vzorc\u00EDch zat\u011B\u017Eovan\u00FDch do lomu."@cs . . . "N\u00EDzkocyklov\u00E1 \u00FAnava lit\u00E9 superslitiny Inconel 738LC p\u0159i vysok\u00E9 teplot\u011B"@cs . .