"A Comparative Study of TiO2-supported and Bulk Co-Mn-Al Catalysts for N2O Decomposition" . "NL - Nizozemsko" . . "Mat\u011Bjka, V." . . "191" . . "A Comparative Study of TiO2-supported and Bulk Co-Mn-Al Catalysts for N2O Decomposition"@en . . . "I, P(GA106/09/1664), Z(MSM6198910016)" . "RIV/67985858:_____/12:00398558" . "Obalov\u00E1, L." . "A series of Co-Mn-Al/TiO2 catalysts with different Co+Mn loading (5-24 wt%) was prepared by impregnation of TiO2 support. Bulk Co-Mn-Al mixed oxides were prepared by different methods. TiO2 acted as a catalytic support and did not contribute to the catalytic activity. The N2O conversion over TiO2-supported Co-Mn-Al catalyst was increasing with Co+Mn loading, and was proportional to the amount of easily reducible components. The highest catalytic activity was achieved on the calcined precursors having carbonates in their molecules." . "[36D1101CF532]" . . . "\u0160tudentov\u00E1, S." . . "nitrous oxide; catalytic decomposition; layered double hydroxides"@en . "Catalysis Today" . "0920-5861" . "000308675000019" . . . "A series of Co-Mn-Al/TiO2 catalysts with different Co+Mn loading (5-24 wt%) was prepared by impregnation of TiO2 support. Bulk Co-Mn-Al mixed oxides were prepared by different methods. TiO2 acted as a catalytic support and did not contribute to the catalytic activity. The N2O conversion over TiO2-supported Co-Mn-Al catalyst was increasing with Co+Mn loading, and was proportional to the amount of easily reducible components. The highest catalytic activity was achieved on the calcined precursors having carbonates in their molecules."@en . . . "4"^^ . "Kar\u00E1skov\u00E1, K." . . "Jir\u00E1tov\u00E1, Kv\u011Bta" . . "A Comparative Study of TiO2-supported and Bulk Co-Mn-Al Catalysts for N2O Decomposition" . "Chrom\u010D\u00E1kov\u00E1, \u017D." . . "1"^^ . "RIV/67985858:_____/12:00398558!RIV14-GA0-67985858" . . . "A Comparative Study of TiO2-supported and Bulk Co-Mn-Al Catalysts for N2O Decomposition"@en . "10.1016/j.cattod.2012.03.046" . "1" . . "120077" . . "6"^^ .