. "Zp\u016Fsob v\u00FDroby syntetick\u00E9 strusky"@cs . "\u00DA\u0159ad pr\u016Fmyslov\u00E9ho vlastnictv\u00ED" . . "Zp\u016Fsob v\u00FDroby syntetick\u00E9 strusky" . "298914" . "Zp\u016Fsob v\u00FDroby syntetick\u00E9 strusky, ur\u010Den\u00E9 p\u0159edev\u0161\u00EDm pro desulfuraci oceli, je zalo\u017Een na p\u0159\u00EDprav\u011B sm\u011Bsi obsahuj\u00EDc\u00ED krom\u011B hlinitanov\u00E9 suroviny a v\u00E1pence tak\u00E9 hlinitanov\u00FD cement a vodu. P\u0159i prov\u00E1d\u011Bn\u00ED zp\u016Fsobu se nejprve sm\u00EDs\u00ED hlinitanov\u00E1 surovina , v\u00E1penec, hlinitanov\u00FD cement a voda v hmotnostn\u00EDm pom\u011Bru Al2O3:CaO rovn\u00E9m 0,8 : 1 a\u017E 1,6 : 1, p\u0159i\u010Dem\u017E obsah hlinitanov\u00E9ho cementu ve sm\u011Bsi je 2 a\u017E 16 % hmotn. a obsah vody ve sm\u011Bsi je 2 a\u017E 30 % hmotn., pak se vznikl\u00E1 sm\u011Bs podrob\u00ED aglomeraci a aglomer\u00E1ty se kalcinuj\u00ED p\u0159i teplot\u011B 1250 a\u017E 1340 \u00B0C, \u010D\u00EDm\u017E je z\u00EDsk\u00E1na syntetick\u00E1 struska s dominantn\u00EDm obsahem f\u00E1ze 12CaO.7Al2O3 (mayenitu)."@cs . . . "[1B3C542FDDE8]" . "2"^^ . . "2008-01-30+01:00"^^ . . "2"^^ . "Zp\u016Fsob v\u00FDroby syntetick\u00E9 strusky" . . "Prague" . . . "407313" . . "The invented process for producing synthetic slag, intended particularly for steel desulphurization, is based on preparation of a mixture containing in addition to alumina starting material and limestone also aluminous cement and water. The process is characterized by mixing the alumina starting material, limestone, aluminous cement and water in weight ratio Ali2Oi3 : CaO = 0.8 : 1 to 1.6 : 1, whereby the amount of the aluminous cement in the mixture ranges within 2 to 16 percent by weight and water content in the mixture is in then range of 2 to 30 percent by weight. Subsequently, the obtained mixture is subjected to agglomeration and agglomerates are calcined at a temperature ranging from 1250 to 1340 degC, to thereby obtain a synthetic slag with dominant amount of the 12CaO.7Ali2Oi3 phase (i.e. mayenite)"@en . "Koutn\u00EDk, Petr" . . . "Posledn\u00ED, Marina" . . . "http://spisy.upv.cz/Patents/FullDocuments/298/298914.pdf" . . "RIV/62243136:_____/08:#0000169!RIV12-MPO-62243136" . . . . "slag, synthetic slag, alumina, limestone, alumina cement"@en . . "P(FI-IM2/089)" . . "Process for producing synthetic slag"@en . . . "Zp\u016Fsob v\u00FDroby syntetick\u00E9 strusky, ur\u010Den\u00E9 p\u0159edev\u0161\u00EDm pro desulfuraci oceli, je zalo\u017Een na p\u0159\u00EDprav\u011B sm\u011Bsi obsahuj\u00EDc\u00ED krom\u011B hlinitanov\u00E9 suroviny a v\u00E1pence tak\u00E9 hlinitanov\u00FD cement a vodu. P\u0159i prov\u00E1d\u011Bn\u00ED zp\u016Fsobu se nejprve sm\u00EDs\u00ED hlinitanov\u00E1 surovina , v\u00E1penec, hlinitanov\u00FD cement a voda v hmotnostn\u00EDm pom\u011Bru Al2O3:CaO rovn\u00E9m 0,8 : 1 a\u017E 1,6 : 1, p\u0159i\u010Dem\u017E obsah hlinitanov\u00E9ho cementu ve sm\u011Bsi je 2 a\u017E 16 % hmotn. a obsah vody ve sm\u011Bsi je 2 a\u017E 30 % hmotn., pak se vznikl\u00E1 sm\u011Bs podrob\u00ED aglomeraci a aglomer\u00E1ty se kalcinuj\u00ED p\u0159i teplot\u011B 1250 a\u017E 1340 \u00B0C, \u010D\u00EDm\u017E je z\u00EDsk\u00E1na syntetick\u00E1 struska s dominantn\u00EDm obsahem f\u00E1ze 12CaO.7Al2O3 (mayenitu)." . . "Zp\u016Fsob v\u00FDroby syntetick\u00E9 strusky"@cs . "Process for producing synthetic slag"@en . "V\u00FDzkumn\u00FD \u00FAstav anorganick\u00E9 chemie, a.s., \u00DAst\u00ED nad Labem; \u010Cesk\u00E9 lupkov\u00E9 z\u00E1vody, a.s., Nov\u00E9 Stra\u0161ec\u00ED" . "RIV/62243136:_____/08:#0000169" . .