"\u00DAnavov\u00E9 lomy jsou nej\u010Dast\u011Bj\u0161\u00ED p\u0159\u00ED\u010Dinou havarijn\u00EDch poruch stroj\u016F a za\u0159\u00EDzen\u00ED. P\u0159i cyklick\u00E9m zat\u00ED\u017Een\u00ED se lom \u0161\u00ED\u0159\u00ED p\u0159ednostn\u011B od povrchu sou\u010D\u00E1sti z m\u00EDst s nejvy\u0161\u0161\u00ED koncentrac\u00ED tahov\u00E9ho nap\u011Bt\u00ED. P\u0159\u00EDtomnost trhlinek, vm\u011Bstk\u016F i drsn\u00FD povrch sou\u010D\u00E1sti sni\u017Euj\u00ED mez \u00FAnavy. \u010Cl\u00E1nek monitoruje \u0161\u00ED\u0159en\u00ED trhlinek ve svaru a tepeln\u011B ovlivn\u011Bn\u00E9m p\u00E1smu p\u0159i \u00FAnavov\u00FDch zkou\u0161k\u00E1ch. Porovn\u00E1v\u00E1 zku\u0161ebn\u00ED vzorky nezkorodovan\u00E9 se vzorky, kter\u00E9 byly vystaveny korozn\u00EDmu p\u016Fsoben\u00ED v soln\u00E9 komo\u0159e."@cs . . "CZ - \u010Cesk\u00E1 republika" . . "Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis" . "Vliv koroze na \u00FAnavovou pevnost svarov\u00E9ho spoje" . "RIV/62156489:43210/07:00111392!RIV08-MSM-43210___" . "1;9" . "3"^^ . . . "3"^^ . . . "Fil\u00EDpek, Josef" . "Vliv koroze na \u00FAnavovou pevnost svarov\u00E9ho spoje"@cs . "Vliv koroze na \u00FAnavovou pevnost svarov\u00E9ho spoje" . "9"^^ . . "v tisku" . "458385" . . . . "." . . "Vliv koroze na \u00FAnavovou pevnost svarov\u00E9ho spoje"@cs . "The fatigue fractures represent the most frequent failure cause of the machines and machinery in general. Under cycling loading, the fracture is mainly propagating from the surface of the part -- the place with highest value of stress concentration. Fatigue strength is decreased by presence of the cracks, inclusions and rugged surface. The paper is focused on monitoring of the crack propagation in weld and heat-affected zone during the fatigue test. Comparison of corrosion-free test samples and samples treated in the salt cabinet is presented."@en . . "Z(MSM6215648905)" . . "Influence of corrosion on the fatigue strength of the weld joint"@en . "43210" . "\u010Cern\u00FD, Michal" . . "\u0160och, Zbyn\u011Bk" . "\u00DAnavov\u00E9 lomy jsou nej\u010Dast\u011Bj\u0161\u00ED p\u0159\u00ED\u010Dinou havarijn\u00EDch poruch stroj\u016F a za\u0159\u00EDzen\u00ED. P\u0159i cyklick\u00E9m zat\u00ED\u017Een\u00ED se lom \u0161\u00ED\u0159\u00ED p\u0159ednostn\u011B od povrchu sou\u010D\u00E1sti z m\u00EDst s nejvy\u0161\u0161\u00ED koncentrac\u00ED tahov\u00E9ho nap\u011Bt\u00ED. P\u0159\u00EDtomnost trhlinek, vm\u011Bstk\u016F i drsn\u00FD povrch sou\u010D\u00E1sti sni\u017Euj\u00ED mez \u00FAnavy. \u010Cl\u00E1nek monitoruje \u0161\u00ED\u0159en\u00ED trhlinek ve svaru a tepeln\u011B ovlivn\u011Bn\u00E9m p\u00E1smu p\u0159i \u00FAnavov\u00FDch zkou\u0161k\u00E1ch. Porovn\u00E1v\u00E1 zku\u0161ebn\u00ED vzorky nezkorodovan\u00E9 se vzorky, kter\u00E9 byly vystaveny korozn\u00EDmu p\u016Fsoben\u00ED v soln\u00E9 komo\u0159e." . . "RIV/62156489:43210/07:00111392" . "Influence of corrosion on the fatigue strength of the weld joint"@en . "corrosion; fatigue fracture; weld joint; cyclic loading"@en . . . "[2CD3BD512CB3]" . "1211-8516" . .