"Catalysis Today" . "Vliv mol\u00E1rn\u00EDho pom\u011Bru Mn/Al v katalyz\u00E1torech p\u0159ipraven\u00FDch kalcinac\u00ED Co-Mn-Al hydrotalcit\u016F na katalytick\u00FD rozklad N2O"@cs . "Effect of Mn/Al ratio in Co-Mn-Al catalysts prepared from hydrotalcite-like precursors on catalytic decomposition of N2O"@en . "The Co-Mn-Al mixed oxide catalysts were prepared by thermal decomposition of hydrotalcite-like precursors with Co/(Mn+Al) molar ratio of 2 and Mn/Al molar ratio varying from 0 to 2. The obtained catalysts were characterized by powder XRD, XPS, BET surface area and TPR measurements and tested in N2O decomposition. The most active Co4MnAl catalyst exhibited both the optimum Mn/Al molar ratio and the optimum amount of components reducible in the temperature region in which the catalytic reaction proceeds (350-450 \u00B0C)."@en . . "119" . . "0920-5861" . "Kovanda, Franti\u0161ek" . "4"^^ . . . "1-4" . . . "Bastl, Z." . "BE - Belgick\u00E9 kr\u00E1lovstv\u00ED" . "Jir\u00E1tov\u00E1, Kv\u011Btu\u0161e" . "Vliv mol\u00E1rn\u00EDho pom\u011Bru Mn/Al v katalyz\u00E1torech p\u0159ipraven\u00FDch kalcinac\u00ED Co-Mn-Al hydrotalcit\u016F na katalytick\u00FD rozklad N2O"@cs . "Lacn\u00FD, Zdenek" . . "P(GA104/04/2116), P(GA106/05/0366), Z(AV0Z40400503), Z(AV0Z40720504), Z(MSM6046137302), Z(MSM6198910016)" . . . "Effect of Mn/Al ratio in Co-Mn-Al catalysts prepared from hydrotalcite-like precursors on catalytic decomposition of N2O"@en . . . . "Obalov\u00E1, Lucie" . . "Balab\u00E1nov\u00E1, J." . . . . "[026D5BF03EC8]" . . "Pacultov\u00E1, Kate\u0159ina" . "N2O decomposition; Mixed oxide catalysts; Hydrotalcite-like compounds"@en . . "RIV/61989100:27360/07:00014095" . "Effect of Mn/Al ratio in Co-Mn-Al catalysts prepared from hydrotalcite-like precursors on catalytic decomposition of N2O" . "Effect of Mn/Al ratio in Co-Mn-Al catalysts prepared from hydrotalcite-like precursors on catalytic decomposition of N2O" . . . . "RIV/61989100:27360/07:00014095!RIV09-MSM-27360___" . . "419010" . . "8"^^ . . "The Co-Mn-Al mixed oxide catalysts were prepared by thermal decomposition of hydrotalcite-like precursors with Co/(Mn+Al) molar ratio of 2 and Mn/Al molar ratio varying from 0 to 2. The obtained catalysts were characterized by powder XRD, XPS, BET surface area and TPR measurements and tested in N2O decomposition. The most active Co4MnAl catalyst exhibited both the optimum Mn/Al molar ratio and the optimum amount of components reducible in the temperature region in which the catalytic reaction proceeds (350-450 \u00B0C)." . "\u010Cl\u00E1nek se zab\u00FDv\u00E1 katalytick\u00FDm rozkladem N2O na katalyz\u00E1torech p\u0159ipraven\u00FDch kalcinac\u00ED Co-Mn-Al hydrotalcitov\u00FDch prekurzor\u016F s mol\u00E1rn\u00EDm pom\u011Brem Co/(Mn+Al)=2 a mol\u00E1rn\u00EDm pom\u011Brem Mn/Al m\u011Bn\u00EDc\u00EDm se od 0 do 2. P\u0159ipraven\u00E9 katalyz\u00E1tory byly charakterizov\u00E1ny pomoc\u00ED RTG a XPS anal\u00FDzy, byl stanoven m\u011Brn\u00FD povrch (BET), byla provedena TPR a sledov\u00E1na katalytick\u00E1 aktivita pro rozklad N2O. Jako nejaktivn\u011Bj\u0161\u00ED katalyz\u00E1tor byl vyhodnocen vzorek, kter\u00FD obsahoval jak optim\u00E1ln\u00ED pom\u011Br Mn/Al, tak optim\u00E1ln\u00ED mno\u017Estv\u00ED slo\u017Eek redukovateln\u00FDch v teplotn\u00EDm intervalu, ve kter\u00E9m prob\u00EDhal katalytick\u00FD rozklad (350-450 \u00B0C)."@cs . "6"^^ . "Val\u00E1\u0161kov\u00E1, Marta" . "27360" .