"2"^^ . "[2768DACAFEF9]" . "Determination of softening degree during static recrystallization"@en . . "RIV/61989100:27360/05:00012941" . "2"^^ . "12. mezin\u00E1rodn\u00ED konference FORMING 2005" . "Stanoven\u00ED stupn\u011B uzdraven\u00ED X p\u0159i statick\u00E9 rekrystalizaci"@cs . "Lednice" . . . "Kliber, Ji\u0159\u00ED" . "119-122" . . . . "Vysok\u00E1 \u0161kola b\u00E1\u0148sk\u00E1 - Technick\u00E1 univerzita Ostrava" . . . "80-248-0888-9" . . . "Plastometrick\u00FDmi zkou\u0161kami je sledov\u00E1na statick\u00E1 rekrystalizace v tv\u00E1\u0159en\u00E9m materi\u00E1lu . Vytvo\u0159en\u00FD model je v z\u00E1vislosti na \u010Dase, teplot\u011B a rychlosti deformace a je z\u00EDsk\u00E1n na z\u00E1klad\u011B stupn\u011B zm\u011Bk\u010Den\u00ED X. Tato hodnota se po\u010D\u00EDt\u00E1 bez nutn\u00E9 znalosti aktiva\u010Dn\u00ED energie. V\u00FDsledn\u00E9 vztahy neuva\u017Euj\u00ED p\u0159edch\u00E1zej\u00EDc\u00ED statick\u00E9 zotaven\u00ED."@cs . . "P(GA106/04/0601), Z(MSM6198910015)" . . "Stanoven\u00ED stupn\u011B uzdraven\u00ED X p\u0159i statick\u00E9 rekrystalizaci" . "Stanoven\u00ED stupn\u011B uzdraven\u00ED X p\u0159i statick\u00E9 rekrystalizaci" . "Stanoven\u00ED stupn\u011B uzdraven\u00ED X p\u0159i statick\u00E9 rekrystalizaci"@cs . "Determination of softening degree during static recrystallization"@en . . . "Ostrava" . "27360" . "4"^^ . "544401" . "2005-09-14+02:00"^^ . "RIV/61989100:27360/05:00012941!RIV06-MSM-27360___" . "Static recrystallization has been investigated in metal material through the use of plastometric tests. The static model is expressed as a function of time t, temperature T and strain rate obtained from experimental X curves. Fractional softening X is calculated without in general essential assignation and knowledge of activation energy Q. The whole advancement does not cover the static recovery on the beginning of softening."@en . "Static recrystallization; softening ratio X; plastometric experiment"@en . "Plastometrick\u00FDmi zkou\u0161kami je sledov\u00E1na statick\u00E1 rekrystalizace v tv\u00E1\u0159en\u00E9m materi\u00E1lu . Vytvo\u0159en\u00FD model je v z\u00E1vislosti na \u010Dase, teplot\u011B a rychlosti deformace a je z\u00EDsk\u00E1n na z\u00E1klad\u011B stupn\u011B zm\u011Bk\u010Den\u00ED X. Tato hodnota se po\u010D\u00EDt\u00E1 bez nutn\u00E9 znalosti aktiva\u010Dn\u00ED energie. V\u00FDsledn\u00E9 vztahy neuva\u017Euj\u00ED p\u0159edch\u00E1zej\u00EDc\u00ED statick\u00E9 zotaven\u00ED." . . . . "Fab\u00EDk, Richard" . . .