"111-114" . . "Mechanika Nr 290/2003" . "Vybran\u00E9 odl\u00E9van\u00E9 kolo ze slitiny AZ91 je n\u00E1chyln\u00E9 ke korozn\u00EDmu prask\u00E1n\u00ED v prost\u0159ed\u00ED \u010Dist\u00E9 vody. Za dan\u00FDch zku\u0161ebn\u00EDch podm\u00EDnek (nap\u011Bt\u00ED 60-150 MPa, pokojov\u00E1 teplota) byla nam\u011B\u0159ena deformace AZ91 p\u0159i te\u010Den\u00ED v rozmez\u00ED 0,01-0,1%, p\u0159itom nebyl zji\u0161t\u011Bn jev korozn\u00EDho te\u010Den\u00ED. Korozn\u00ED trhliny se \u0161\u00ED\u0159ily transkrystalick\u00FDm kvazik\u0159ehk\u00FDm mechanismem." . . . . "The tested cast car wheel of alloy AZ91 is susceptible to stress corrosion cracking in pure water. Under testing conditions (tensile stress 60-150 MPa, room temperature) the creep deformation (0,01-0,1%) was measured, but corrosion creep phenomenon was not found. The transcrystalline corrosion quasicleveage cracks were observed by SEM."@en . . "P\u0159\u00EDsp\u011Bvek ke studiu korozn\u00EDho prask\u00E1n\u00ED slitiny AZ91"@en . . "Lasek, Stanislav" . "RIV/61989100:27360/03:00009342" . . "3"^^ . "P\u0159\u00EDsp\u011Bvek ke studiu korozn\u00EDho prask\u00E1n\u00ED slitiny AZ91"@en . "P(GA106/01/1247)" . "1429-6055" . "RIV/61989100:27360/03:00009342!RIV/2004/GA0/273604/N" . . . "27360" . "P\u0159\u00EDsp\u011Bvek ke studiu korozn\u00EDho prask\u00E1n\u00ED slitiny AZ91" . "Magnesium alloy AZ91, stress corrosion crack., creep,"@en . "\u010C\u00ED\u017Eek, Lubom\u00EDr" . "P\u0159\u00EDsp\u011Bvek ke studiu korozn\u00EDho prask\u00E1n\u00ED slitiny AZ91"@cs . "0"^^ . "4"^^ . "0"^^ . "[67491E2E1107]" . "Blahetov\u00E1, Marie" . . . "76" . "290" . . "6"^^ . . "623211" . "PL - Polsk\u00E1 republika" . . . "Ludv\u00EDkova, I." . "P\u0159\u00EDsp\u011Bvek ke studiu korozn\u00EDho prask\u00E1n\u00ED slitiny AZ91" . . . "P\u0159\u00EDsp\u011Bvek ke studiu korozn\u00EDho prask\u00E1n\u00ED slitiny AZ91"@cs .