. "P(GBP108/12/G043), P(KAN300100801)" . "Kovov\u00E9 Materi\u00E1ly-Metallic Materials" . "Characterization of the Al-13Si-10Fe alloy produced by centrifugal atomization and ultra-high-pressure compaction" . "D\u00E1m, Karel" . "An Al-13Si-10Fe (wt. %) alloy was prepared via melt centrifugal atomization and compaction at a pressure of 6 GPa. The compact was porosity-free with good contacts between particles. The structure was very fine and consisted of primary a(Al) dendrites, eutectic silicon and needles of the b-Al5FeSi phase. The Vickers hardness and compressive strength were 185 HV and 720 MPa, respectively. Surprisingly, the as-compacted alloy exhibited a certain degree of plasticity due to the refined morphology of needles." . "Vojt\u011Bch, Dalibor" . "22310" . . . . . "000313460300005" . "Characterization of the Al-13Si-10Fe alloy produced by centrifugal atomization and ultra-high-pressure compaction"@en . . . . . "50" . "0023-432X" . "126843" . . . "RIV/60461373:22310/12:43894499!RIV13-GA0-22310___" . "Pr\u016F\u0161a, Filip" . "mechanical properties; structure; rapid solidification; Al-Si-Fe alloy; aluminium"@en . "RIV/60461373:22310/12:43894499" . "An Al-13Si-10Fe (wt. %) alloy was prepared via melt centrifugal atomization and compaction at a pressure of 6 GPa. The compact was porosity-free with good contacts between particles. The structure was very fine and consisted of primary a(Al) dendrites, eutectic silicon and needles of the b-Al5FeSi phase. The Vickers hardness and compressive strength were 185 HV and 720 MPa, respectively. Surprisingly, the as-compacted alloy exhibited a certain degree of plasticity due to the refined morphology of needles."@en . "10.4149/km_2012_6_399" . "[327A9674601C]" . . . . "Characterization of the Al-13Si-10Fe alloy produced by centrifugal atomization and ultra-high-pressure compaction" . "3"^^ . . . . "6" . "3"^^ . "8"^^ . . "Characterization of the Al-13Si-10Fe alloy produced by centrifugal atomization and ultra-high-pressure compaction"@en . . . . "SK - Slovensk\u00E1 republika" .