. . "22310" . . . "It has been widely accepted that Ag-additives reduce the partial melting temperature and thereby accelerate the formation rate of Bi-2223 phase, reduce porosity, improve the mechanical properties and the weak links connecting superconducting grains. Nano-metric size particles have diameters in some range as magnetic pinning centers in the HTS. The influence of the nanometer Ag particles on Bi-2223 phase formation, microstructure and transport properties of samples have been studied. Samples with nominal composition Bi3.2Pb0.8Sr4Ca5Cu7Ox were prepared by solid state synthesis. Ag was used in three different weight percentage 5, 10 and 15. Ag powder was added to the initial mixture or after second calcination." . . "2"^^ . "It has been widely accepted that Ag-additives reduce the partial melting temperature and thereby accelerate the formation rate of Bi-2223 phase, reduce porosity, improve the mechanical properties and the weak links connecting superconducting grains. Nano-metric size particles have diameters in some range as magnetic pinning centers in the HTS. The influence of the nanometer Ag particles on Bi-2223 phase formation, microstructure and transport properties of samples have been studied. Samples with nominal composition Bi3.2Pb0.8Sr4Ca5Cu7Ox were prepared by solid state synthesis. Ag was used in three different weight percentage 5, 10 and 15. Ag powder was added to the initial mixture or after second calcination."@en . "Bismutov\u00E9 supravodi\u010De s nano-dopanty"@cs . . "Smr\u010Dkov\u00E1, Olga" . "RIV/60461373:22310/05:00014147" . . "Poster: Bi-based superconductors with nanosize dopants"@en . "2"^^ . "Poster: Bi-based superconductors with nanosize dopants"@en . "P(GA203/05/0114), Z(MSM6046137302)" . "RIV/60461373:22310/05:00014147!RIV06-MSM-22310___" . "Poster: Bi-based superconductors with nanosize dopants" . . . . . . "Bismutov\u00E9 supravodi\u010De s nano-dopanty"@cs . . "[A74D00E6005B]" . . "Bi-based superconductors with nanosize dopants"@en . "537046" . . . "S\u00FDkorov\u00E1, Dagmar" . "Byl sledov\u00E1n vliv p\u0159\u00EDdavku nano\u010D\u00E1stic st\u0159\u00EDbra na transportn\u00ED vlastnosti supravodi\u010De Bi-2223, jeho tvorbu a mikrostrukturu. Reakc\u00ED v pevn\u00E9 f\u00E1zi byly p\u0159ipraveny vzorky stechiometrick\u00E9ho slo\u017Een\u00ED Bi3.2Pb0.8Sr4Ca5Cu7Ox, st\u0159\u00EDbro bylo p\u0159id\u00E1v\u00E1no v mno\u017Estv\u00ED 0, 5 a 10 hm.%."@cs . "Poster: Bi-based superconductors with nanosize dopants" .