"Sledov\u00E1n\u00ED vlastnost\u00ED dvouslo\u017Ekov\u00FDch kompozit\u016F metodou STA"@cs . . "287829" . "Sledov\u00E1n\u00ED vlastnost\u00ED dvouslo\u017Ekov\u00FDch kompozit\u016F metodou STA" . . . . . . "Observation of two component composites properties via simultaneous thermal analysis"@en . "RIV/49777513:23220/10:00504920!RIV11-MSM-23220___" . "4"^^ . . "RIV/49777513:23220/10:00504920" . "Tento \u010Dl\u00E1nek se zab\u00FDv\u00E1 vlivem zrychlen\u00E9ho tepeln\u00E9ho st\u00E1rnut\u00ED na vlastnosti reaktoplastick\u00E9ho epoxidov\u00E9ho lamin\u00E1tu. Materi\u00E1l byl vystaven \u00FA\u010Dink\u016Fm tepeln\u00E9ho nam\u00E1h\u00E1n\u00ED v hladin\u00E1ch 170 a\u017E 200 \u00B0C p\u0159i dob\u00E1ch expozice 10 a\u017E 480 hodin. Vzorky byly analyzov\u00E1ny pomoc\u00ED simult\u00E1nn\u00EDho termick\u00E9ho analyz\u00E1toru - SDT Q600. Na termogramu diferen\u010Dn\u00ED skenovan\u00ED kalorimetrie byl sledov\u00E1n skeln\u00FD p\u0159echod a lok\u00E1ln\u00ED teplotn\u00ED maximum v oblasti termooxidace. Pomoc\u00ED termogravimetrick\u00E9 anal\u00FDzy byl sledov\u00E1n trend hmotnostn\u00EDch \u00FAbytk\u016F v oblasti 300 a\u017E 340 \u00B0C. Z v\u00FDsledk\u016F anal\u00FDz byly zhotoveny \u017Eivotnostn\u00ED k\u0159ivky a vynesena jejich vz\u00E1jemn\u00E1 korelace s \u017Eivotnostn\u00ED k\u0159ivkou z\u00EDskanou fenomenologick\u00FDm p\u0159\u00EDstupem." . "4"^^ . "Sledov\u00E1n\u00ED vlastnost\u00ED dvouslo\u017Ekov\u00FDch kompozit\u016F metodou STA"@cs . . . . "Sledov\u00E1n\u00ED vlastnost\u00ED dvouslo\u017Ekov\u00FDch kompozit\u016F metodou STA" . . . "Polansk\u00FD, Radek" . . "Mentl\u00EDk, V\u00E1clav" . . "Su\u0161\u00EDr, Josef" . "Prosr, Pavel" . "This article deals with the influence of accelerated thermal ageing on thermosetting epoxy laminate properties. The material was exposed to thermal stress from 170 to 200 \u00B0C (from 10 to 480 hours). Samples were analyzed by the help of simultaneous thermal analyzer ? SDT Q600. These both glass transition temperature and local peak of thermal-oxidative process were investigated via differential scanning calorimetry. Weight losses were analyzed by thermogravimetry analysis at temperatures ranging from 300 to 340 \u00B0C. Lifetime curves were calculated from all results and cross-correlation of lifetime curves between thermal analyses and phenomenological methods results was made."@en . "[16D3DB5600FE]" . . . . "23220" . "Observation of two component composites properties via simultaneous thermal analysis"@en . . . "Z(MSM4977751310)" . "Tento \u010Dl\u00E1nek se zab\u00FDv\u00E1 vlivem zrychlen\u00E9ho tepeln\u00E9ho st\u00E1rnut\u00ED na vlastnosti reaktoplastick\u00E9ho epoxidov\u00E9ho lamin\u00E1tu. Materi\u00E1l byl vystaven \u00FA\u010Dink\u016Fm tepeln\u00E9ho nam\u00E1h\u00E1n\u00ED v hladin\u00E1ch 170 a\u017E 200 \u00B0C p\u0159i dob\u00E1ch expozice 10 a\u017E 480 hodin. Vzorky byly analyzov\u00E1ny pomoc\u00ED simult\u00E1nn\u00EDho termick\u00E9ho analyz\u00E1toru - SDT Q600. Na termogramu diferen\u010Dn\u00ED skenovan\u00ED kalorimetrie byl sledov\u00E1n skeln\u00FD p\u0159echod a lok\u00E1ln\u00ED teplotn\u00ED maximum v oblasti termooxidace. Pomoc\u00ED termogravimetrick\u00E9 anal\u00FDzy byl sledov\u00E1n trend hmotnostn\u00EDch \u00FAbytk\u016F v oblasti 300 a\u017E 340 \u00B0C. Z v\u00FDsledk\u016F anal\u00FDz byly zhotoveny \u017Eivotnostn\u00ED k\u0159ivky a vynesena jejich vz\u00E1jemn\u00E1 korelace s \u017Eivotnostn\u00ED k\u0159ivkou z\u00EDskanou fenomenologick\u00FDm p\u0159\u00EDstupem."@cs . "Thermogravimetric analysis; Differential scanning calorimetry; Thermal stress; Printed circuit board; Glass transition temperature"@en . .