. . . . . . "TRIP steels represent modern group of low alloyed steels which allow reaching of excellent combination of strength and ductility. For their treatment by unconventional forming methods and with regards to possibility to use the TRIP effect at final cold forming not only the very fine structure has to be obtained but also sufficient fraction of phases. Structure development can be intensively affected by appropriate temperature interval of incremental deformation and its size. In experimental program the influence of 20 step deformation in various temperature intervals and the influence of different deformation size on structure refinement were investigated. At the suitable chosen parameters the ferrite-bainite structure with 15% of retained austenite, size of ferrite grain of about 2 um and ductility of about 30% was obtained."@en . "Vienna" . . "4"^^ . . . "P(1M06032)" . "Refinement of TRIP steel microstructure by incremental deformation"@en . . "2"^^ . "RIV/49777513:23210/11:43897076" . "226110" . "1726-9679" . "Refinement of TRIP steel microstructure by incremental deformation" . "3"^^ . "Meyer, Lothar W." . "[649B9C317CB8]" . . "DAAAM International Vienna 2011" . "Ku\u010Derov\u00E1, Ludmila" . "Refinement of TRIP steel microstructure by incremental deformation"@en . . . "Annals of DAAAM for 2011 & Proceedings of the 22nd international DAAAM symposium" . . "Refinement of TRIP steel microstructure by incremental deformation" . "thermomechanical treatment; incremental deformation; TRIP steel; multiphase steel"@en . "RIV/49777513:23210/11:43897076!RIV14-MSM-23210___" . . . "TRIP steels represent modern group of low alloyed steels which allow reaching of excellent combination of strength and ductility. For their treatment by unconventional forming methods and with regards to possibility to use the TRIP effect at final cold forming not only the very fine structure has to be obtained but also sufficient fraction of phases. Structure development can be intensively affected by appropriate temperature interval of incremental deformation and its size. In experimental program the influence of 20 step deformation in various temperature intervals and the influence of different deformation size on structure refinement were investigated. At the suitable chosen parameters the ferrite-bainite structure with 15% of retained austenite, size of ferrite grain of about 2 um and ductility of about 30% was obtained." . . "Ma\u0161ek, Bohuslav" . "978-3-901509-83-4" . . "23210" . . . "Vienna, Austr\u00E1lie" . "2011-11-23+01:00"^^ . "Jirkov\u00E1, Hana" .