. . . "RIV/47718684:_____/05:#0000024!RIV06-GA0-47718684" . . . "P(GA106/03/0473)" . "lit\u00E1 manganov\u00E1 ocel" . . "Production of advanced cast manganesse microalloying steel for thinwalled casting"@en . . "RIV/47718684:_____/05:#0000024" . "550092" . . "\u0160KODA V\u00DDZKUM, s.r.o." . "[4437B7CFEE05]" . "Production of advanced cast manganesse microalloying steel for thinwalled casting"@en . "1"^^ . "Ocel s obsahem 0,15 C a 1,2 Mn byla mikrolegov\u00E1na vanadem a niobem a podrobena tepeln\u00E9mu zpracov\u00E1n\u00ED skl\u00E1daj\u00EDc\u00EDmu se z normaliza\u010Dn\u00EDho \u017E\u00EDh\u00E1n\u00ED, interkritick\u00E9ho kalen\u00ED a popou\u0161t\u011Bn\u00ED. Bylo dosa\u017Eeno zv\u00FD\u0161en\u00ED meze kluzu (477 MPa) a meze pevnosti (650 MPa) o asi 100 MPa p\u0159i sou\u010Dasn\u00E9m m\u00EDrn\u00E9m zlep\u0161en\u00ED k\u0159ehkolomov\u00FDch vlastnost\u00ED (pokles transitn\u00ED teploty FATT 50 na -5 \u00B0C) v\u016F\u010Di referen\u010Dn\u00ED oceli \u010CSN 42 2707."@cs . "Ocel s obsahem 0,15 C a 1,2 Mn byla mikrolegov\u00E1na vanadem a niobem a podrobena tepeln\u00E9mu zpracov\u00E1n\u00ED skl\u00E1daj\u00EDc\u00EDmu se z normaliza\u010Dn\u00EDho \u017E\u00EDh\u00E1n\u00ED, interkritick\u00E9ho kalen\u00ED a popou\u0161t\u011Bn\u00ED. Bylo dosa\u017Eeno zv\u00FD\u0161en\u00ED meze kluzu (477 MPa) a meze pevnosti (650 MPa) o asi 100 MPa p\u0159i sou\u010Dasn\u00E9m m\u00EDrn\u00E9m zlep\u0161en\u00ED k\u0159ehkolomov\u00FDch vlastnost\u00ED (pokles transitn\u00ED teploty FATT 50 na -5 \u00B0C) v\u016F\u010Di referen\u010Dn\u00ED oceli \u010CSN 42 2707." . "V\u00FDroba lit\u00E9 manganov\u00E9 mikrolegovan\u00E9 oceli pro tenkost\u011Bnn\u00E9 odlitky se zv\u00FD\u0161en\u00FDmi mechanick\u00FDmi vlastnostmi" . "Sn\u00ED\u017Een\u00ED hmotnosti v\u00FDrobku" . . . . "V\u00FDroba lit\u00E9 manganov\u00E9 mikrolegovan\u00E9 oceli pro tenkost\u011Bnn\u00E9 odlitky se zv\u00FD\u0161en\u00FDmi mechanick\u00FDmi vlastnostmi" . "V\u00FDroba lit\u00E9 manganov\u00E9 mikrolegovan\u00E9 oceli pro tenkost\u011Bnn\u00E9 odlitky se zv\u00FD\u0161en\u00FDmi mechanick\u00FDmi vlastnostmi"@cs . "microalloying steel, intercritical heat treatment"@en . "The steel containing 0.15 C and 1.2 Mn was microalloyed by vanadium and niobium was undergone the heta tratment consisting of from homogenizing, normalizing intercritical quenching and tempering. Yield stress (477MPa) and tensile strength (650MPa) increased of about 100 MPa in comparison to reference steel \u010CSN 42 2707 while transition temperature FATT 50 rather decreased."@en . "Lit\u00E1 manganov\u00E1 ocel se zv\u00FD\u0161en\u00FDmi pevnostn\u00EDmi a k\u0159ehkolomov\u00FDmi vlastnostmi. Ve srovn\u00E1n\u00ED se standardn\u00ED ocel\u00ED typu \u010CSN 42 2707ocel vykazuje vy\u0161\u0161\u00ED mez kluzu a pevnosti o 100 Mpa p\u0159i zachov\u00E1n\u00ED hou\u017Eevnatosti a m\u00EDrn\u00E9m zlep\u0161en\u00ED p\u0159echodov\u00E9 teploty" . "V\u00FDroba lit\u00E9 manganov\u00E9 mikrolegovan\u00E9 oceli pro tenkost\u011Bnn\u00E9 odlitky se zv\u00FD\u0161en\u00FDmi mechanick\u00FDmi vlastnostmi"@cs . "Kasl, Josef" . . "1"^^ . . . . .