"Hota\u0159, Vlastimil" . . "Iron aluminides have excellent corrosion resistance over 900\u00B0C. Therefore iron aluminides are possible to use for constructional elements in glass making. Corrosion resistance of Fe3Al - based iron aluminides (with various chemical compositions) was compared with austenitic steel EN X8CrNi25-21 in soda-potash molten glass. The corrosion tests were carried out in laboratory conditions at 1200 \u00B0C and time of interaction was changed. The corrosion resistance all materials were determined by measurement of weight gains, change of surface roughness and change chemical analysis. The tinting of molten glass is interpreted using effect of interaction with alloys."@en . "2"^^ . "Korozn\u00ED odolnost aluminid\u016F \u017Eeleza na b\u00E1zi Fe3Al v sodnov\u00E1penat\u00E9 sklovin\u011B p\u0159i teplot\u011B 1200 \u00B0C."@cs . . "Ostrava" . . "Korozn\u00ED odolnost aluminid\u016F \u017Eeleza na b\u00E1zi Fe3Al v sodnov\u00E1penat\u00E9 sklovin\u011B p\u0159i teplot\u011B 1200 \u00B0C." . . . . "Aluminidy \u017Eeleza maj\u00ED velice dobrou korozn\u00ED odolnost nad teplotou 900\u00B0C. Proto aluminidy \u017Eeleza je mo\u017En\u00E9 pou\u017E\u00EDt na v\u00FDrobu konstruk\u010Dn\u00EDch prvk\u016F ve skl\u00E1\u0159stv\u00ED. Byla porovn\u00E1na korozn\u00ED odolnost aluminid\u016F \u017Eeleza na b\u00E1zi Fe3Al (s r\u016Fzn\u00FDm chemick\u00FDm slo\u017Een\u00EDm) s austenitickou ocel\u00ED EN X8CrNi25-21 v sodnov\u00E1penat\u00E9 sklovin\u011B. Byly provedeny testy v laboratorn\u00EDch podm\u00EDnk\u00E1ch p\u0159i teplot\u011B 1200\u00B0C, kter\u00E9 se li\u0161ily dobou interakce. Korozn\u00ED odolnost v\u0161ech materi\u00E1l\u016F byla stanovena m\u011B\u0159en\u00EDm zm\u011Bny hmotnosti, stanoven\u00EDm zm\u011Bny drsnosti povrchu a chemick\u00E9ho slo\u017Een\u00ED. Vliv interakce skloviny se slitinou byl interpretov\u00E1n zbarven\u00EDm skla." . "P(GP106/05/P167), Z(MSM4674788501)" . . "Tanger s.r.o." . "[0FDF4F546372]" . "6"^^ . . "Aluminidy \u017Eeleza maj\u00ED velice dobrou korozn\u00ED odolnost nad teplotou 900\u00B0C. Proto aluminidy \u017Eeleza je mo\u017En\u00E9 pou\u017E\u00EDt na v\u00FDrobu konstruk\u010Dn\u00EDch prvk\u016F ve skl\u00E1\u0159stv\u00ED. Byla porovn\u00E1na korozn\u00ED odolnost aluminid\u016F \u017Eeleza na b\u00E1zi Fe3Al (s r\u016Fzn\u00FDm chemick\u00FDm slo\u017Een\u00EDm) s austenitickou ocel\u00ED EN X8CrNi25-21 v sodnov\u00E1penat\u00E9 sklovin\u011B. Byly provedeny testy v laboratorn\u00EDch podm\u00EDnk\u00E1ch p\u0159i teplot\u011B 1200\u00B0C, kter\u00E9 se li\u0161ily dobou interakce. Korozn\u00ED odolnost v\u0161ech materi\u00E1l\u016F byla stanovena m\u011B\u0159en\u00EDm zm\u011Bny hmotnosti, stanoven\u00EDm zm\u011Bny drsnosti povrchu a chemick\u00E9ho slo\u017Een\u00ED. Vliv interakce skloviny se slitinou byl interpretov\u00E1n zbarven\u00EDm skla."@cs . . . . "RIV/46747885:24210/08:#0000378" . . . . . "Korozn\u00ED odolnost aluminid\u016F \u017Eeleza na b\u00E1zi Fe3Al v sodnov\u00E1penat\u00E9 sklovin\u011B p\u0159i teplot\u011B 1200 \u00B0C."@cs . "375599" . "2008-01-01+01:00"^^ . . "978-80-254-1987-8" . "Hota\u0159, Adam" . "Metal 2008" . . "Corrosion resistance of Fe3Al \u2013 based iron aluminides in soda-potash molten glass at 1200\u00B0C."@en . "iron aluminide; corrosion; molten glass"@en . "Hradec nad Moravic\u00ED" . "Korozn\u00ED odolnost aluminid\u016F \u017Eeleza na b\u00E1zi Fe3Al v sodnov\u00E1penat\u00E9 sklovin\u011B p\u0159i teplot\u011B 1200 \u00B0C." . "24210" . "2"^^ . "RIV/46747885:24210/08:#0000378!RIV09-GA0-24210___" . . "Corrosion resistance of Fe3Al \u2013 based iron aluminides in soda-potash molten glass at 1200\u00B0C."@en . .