. "Stan\u011Bk, Theodor" . "P(FT-TA/020)" . . . . "Set of laboratory samples of Portland cement with limestone CEM II/A-LL with use of Portland cement clinker with high alumina-iron ratio"@en . . "Lafarge cement, a.s., \u010C\u00ED\u017Ekovice" . "Set of laboratory samples of Portland cement with limestone CEM II/A-LL with use of Portland cement clinker with high alumina-iron ratio"@en . "Prvotn\u00ED optimalizace skladby a jemnosti cementu. U\u0161et\u0159\u00ED se za testov\u00E1n\u00ED a p\u0159istoup\u00ED a\u017E k fin\u00E1ln\u00ED optimalizaci na z\u00E1klad\u011B maloobjemov\u00FDch laboratorn\u00EDch v\u00FDsledk\u016F. V\u00E1penec nahrazuje portlandsk\u00FD sl\u00EDnek a m\u00E1 velmi dobrou melitelnost a nemus\u00ED se kupovat." . . "RIV/26232511:_____/08:CEMNES66" . . "Set of laboratory samples of Portland cement with limestone CEM II/A-LL was prepared. The aim of an examination was to find optimal composition and fineness to achieve good technological properties before impementation of the cement into production. Cements were prepared from Portland cement clinker with high content of tricalciumaluminate, limestone which meets the requirements of \u010CSN EN 197-1 for category LL, fly ash and FGD gypsum. Limestone as the main constituent was added separately in levels of 12 and 20 wt.% or together with 5 wt.% of fly ash as the minor additional constituent. Cements were ground to 2 different specific surfaces. Mixture of Portland cement with 5% of limestone was used as a standard. Preparation set comprised 9 laboratory samples of cement whose weight was 30 kg each."@en . . "2"^^ . . . "Persa\u0148, Vladim\u00EDr" . . "Funk\u010Dn\u00ED vzorek \u2013 soubor zku\u0161ebn\u00EDch vzork\u016F portlandsk\u00FDch cement\u016F s v\u00E1pencem druh CEM II/A-LL p\u0159i pou\u017Eit\u00ED sl\u00EDnku s vysok\u00FDm alumin\u00E1tov\u00FDm modulem"@cs . "RIV/26232511:_____/08:CEMNES66!RIV09-MPO-26232511" . . . "Funk\u010Dn\u00ED vzorek \u2013 soubor zku\u0161ebn\u00EDch vzork\u016F portlandsk\u00FDch cement\u016F s v\u00E1pencem druh CEM II/A-LL p\u0159i pou\u017Eit\u00ED sl\u00EDnku s vysok\u00FDm alumin\u00E1tov\u00FDm modulem"@cs . "blended cement; limestone; tricalciumaluminate"@en . "Zku\u0161ebn\u00ED vzorky cement\u016F spadaj\u00EDc\u00EDch do druhu CEM II/A-LL byly pomlety na 2 r\u016Fzn\u00E9 m\u011Brn\u00E9 povrchy \u2013 400 a 460 m2/kg. V\u0161echny splnily po\u017Eadavky na mechanick\u00E9 a fyzik\u00E1ln\u00ED vlastnosti uveden\u00E9 v \u010CSN EN 197-1 pro pevnostn\u00ED t\u0159\u00EDdu 42,5 R p\u0159\u00EDpadn\u011B 52,5 R." . "2"^^ . . "Funk\u010Dn\u00ED vzorek \u2013 soubor zku\u0161ebn\u00EDch vzork\u016F portlandsk\u00FDch cement\u016F s v\u00E1pencem druh CEM II/A-LL p\u0159i pou\u017Eit\u00ED sl\u00EDnku s vysok\u00FDm alumin\u00E1tov\u00FDm modulem" . "LLCEM1C" . . . . "368766" . "Funk\u010Dn\u00ED vzorek \u2013 soubor zku\u0161ebn\u00EDch vzork\u016F portlandsk\u00FDch cement\u016F s v\u00E1pencem druh CEM II/A-LL p\u0159i pou\u017Eit\u00ED sl\u00EDnku s vysok\u00FDm alumin\u00E1tov\u00FDm modulem" . "Laboratorn\u011B byl p\u0159ipraven soubor portlandsk\u00FDch cement\u016F s v\u00E1pencem druh CEM II/A-LL jako zku\u0161ebn\u00ED testovac\u00ED vzorky pro zji\u0161t\u011Bn\u00ED optim\u00E1ln\u00ED skladby a jemnosti ve vztahu k technologick\u00FDm vlastnostem p\u0159ed zaveden\u00EDm v\u00FDroby tohoto druhu cementu v pr\u016Fmyslov\u00E9m m\u011B\u0159\u00EDtku. Cementy byly p\u0159ipraveny z pr\u016Fmyslov\u00E9ho sl\u00EDnku, kter\u00FD na rozd\u00EDl od b\u011B\u017En\u00FDch sl\u00EDnk\u016F obsahuje velmi vysok\u00FD pod\u00EDl trikalciumalumin\u00E1tu, v\u00E1pence, kter\u00FD spl\u0148uje po\u017Eadavky \u010CSN EN 197-1 pro kategorii LL, elektr\u00E1rensk\u00E9ho pop\u00EDlku a energos\u00E1drovce. V\u00E1penec byl d\u00E1vkov\u00E1n jako hlavn\u00ED slo\u017Eka v mno\u017Estv\u00ED 12 a 20 hm. % a to samostatn\u011B nebo s dopl\u0148uj\u00EDc\u00ED slo\u017Ekou pop\u00EDlek v mno\u017Estv\u00ED 5 hm. %. Cementy byly pomlety na 2 r\u016Fzn\u00E9 m\u011Brn\u00E9 povrchy. Jako srovn\u00E1vac\u00ED standard byl p\u0159ipraven portlandsk\u00FD cement CEM I s dopl\u0148uj\u00EDc\u00ED slo\u017Ekou v\u00E1penec v mno\u017Estv\u00ED 5 hm. %. Celkov\u011B byl p\u0159ipraven soubor 9 zku\u0161ebn\u00EDch vzork\u016F cement\u016F po 30 kg."@cs . . . . "Laboratorn\u011B byl p\u0159ipraven soubor portlandsk\u00FDch cement\u016F s v\u00E1pencem druh CEM II/A-LL jako zku\u0161ebn\u00ED testovac\u00ED vzorky pro zji\u0161t\u011Bn\u00ED optim\u00E1ln\u00ED skladby a jemnosti ve vztahu k technologick\u00FDm vlastnostem p\u0159ed zaveden\u00EDm v\u00FDroby tohoto druhu cementu v pr\u016Fmyslov\u00E9m m\u011B\u0159\u00EDtku. Cementy byly p\u0159ipraveny z pr\u016Fmyslov\u00E9ho sl\u00EDnku, kter\u00FD na rozd\u00EDl od b\u011B\u017En\u00FDch sl\u00EDnk\u016F obsahuje velmi vysok\u00FD pod\u00EDl trikalciumalumin\u00E1tu, v\u00E1pence, kter\u00FD spl\u0148uje po\u017Eadavky \u010CSN EN 197-1 pro kategorii LL, elektr\u00E1rensk\u00E9ho pop\u00EDlku a energos\u00E1drovce. V\u00E1penec byl d\u00E1vkov\u00E1n jako hlavn\u00ED slo\u017Eka v mno\u017Estv\u00ED 12 a 20 hm. % a to samostatn\u011B nebo s dopl\u0148uj\u00EDc\u00ED slo\u017Ekou pop\u00EDlek v mno\u017Estv\u00ED 5 hm. %. Cementy byly pomlety na 2 r\u016Fzn\u00E9 m\u011Brn\u00E9 povrchy. Jako srovn\u00E1vac\u00ED standard byl p\u0159ipraven portlandsk\u00FD cement CEM I s dopl\u0148uj\u00EDc\u00ED slo\u017Ekou v\u00E1penec v mno\u017Estv\u00ED 5 hm. %. Celkov\u011B byl p\u0159ipraven soubor 9 zku\u0161ebn\u00EDch vzork\u016F cement\u016F po 30 kg." . "[B2B5A98ED1BF]" .