"In this article are described results of evaluation and measurement of hydrogen induced cracks and blisters in gas pipeline steels. Quantitative values characterizing hydrogen induced cracking were given into correlation with microstructure. Main reason for susceptibility of these steels to hydrogen induced cracking was found in pearlite banding."@en . . . "Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels"@en . "RIV/25797000:_____/10:#0000216" . "Hydrogen induced cracking; Pipeline steel; Pearlite banding; Microstructure"@en . "Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels"@en . . "Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels" . "5"^^ . . "978-80-87294-17-8" . . . . "Z(MSM2579700001)" . "METAL 2010: 19th International Metallurgical and Materials Conference" . . . . "2010-01-01+01:00"^^ . "In this article are described results of evaluation and measurement of hydrogen induced cracks and blisters in gas pipeline steels. Quantitative values characterizing hydrogen induced cracking were given into correlation with microstructure. Main reason for susceptibility of these steels to hydrogen induced cracking was found in pearlite banding." . "\u010Cipera, Martin" . . . . . "2"^^ . "RIV/25797000:_____/10:#0000216!RIV11-MSM-25797000" . . . . "263708" . "Mikulov\u00E1, Dagmar" . "Ro\u017Enov pod Radho\u0161t\u011Bm, \u010CR" . "2"^^ . "[8AA5FEC7A072]" . "TANGER, spol s r.o." . . "Ostrava, \u010Cesk\u00E1 Republika" . "Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels" .