"39060" . "Preparation of Transparent 3Y-TZP Nanoceramics with No Low-Temperature Degradation" . . . . . . "0002-7820" . . "ZIRCONIA NANOPARTICLES, DENTAL APPLICATIONS, TRANSFORMATIONS, BIOMATERIAL, CERAMICS, ALUMINA, FUTURE"@en . "5"^^ . "The progresses of the relative density, average grain size (GS), and maximum pore size entering into the final sintering stage are investigated in 3 mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP) compacts in the range of 87%~99% theoretical density. It is found that during conventional pressureless sintering, the pores in the compact enlarged dramatically, which appears to be the major obstacle for preparing fully dense nanoceramics. Transparent 3Y-TZP nanoceramics with an average GS of 87 nm were prepared by exploiting microstructural refinement on nanoscale. The yields a maximal optical transmittance of 67% and shows no noticeable low-temperature degradation after 100 h aging at 134 C under a hydrothermal pressure of two bars."@en . "Fu, Zhengyi" . . . "RIV/00216305:26620/14:PU108717!RIV15-MSM-26620___" . "The progresses of the relative density, average grain size (GS), and maximum pore size entering into the final sintering stage are investigated in 3 mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP) compacts in the range of 87%~99% theoretical density. It is found that during conventional pressureless sintering, the pores in the compact enlarged dramatically, which appears to be the major obstacle for preparing fully dense nanoceramics. Transparent 3Y-TZP nanoceramics with an average GS of 87 nm were prepared by exploiting microstructural refinement on nanoscale. The yields a maximal optical transmittance of 67% and shows no noticeable low-temperature degradation after 100 h aging at 134 C under a hydrothermal pressure of two bars." . "Preparation of Transparent 3Y-TZP Nanoceramics with No Low-Temperature Degradation"@en . "Maca, Karel" . "P(ED1.1.00/02.0068)" . "26620" . . "Preparation of Transparent 3Y-TZP Nanoceramics with No Low-Temperature Degradation" . "2"^^ . . "5" . "97" . . . . "Xiong, Yan" . . "5"^^ . "Shen, Zhijian" . "Journal of the American Ceramic Society" . . "RIV/00216305:26620/14:PU108717" . "US - Spojen\u00E9 st\u00E1ty americk\u00E9" . . . "Preparation of Transparent 3Y-TZP Nanoceramics with No Low-Temperature Degradation"@en . "Pouchl\u00FD, V\u00E1clav" . . "[8421E22C2B35]" . . .