. "4"^^ . . . . . "\u0158\u00E1dkov\u00E1, Lucie" . "Fojt\u00EDkov\u00E1, Petra" . "Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy."@en . "101847" . . . "RIV/00216305:26310/13:PU105270" . "Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma"@en . "26310" . "[456F50176750]" . . "Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma" . "model corrosion layers of brass samples, low-pressure low-temperature hydrogen plasma, plasma chemical reduction of corrosion layers"@en . . . "Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy." . "4"^^ . "S\u00E1zavsk\u00E1, V\u011Bra" . . . . . . . "Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma"@en . . . "Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma" . . "P(DF11P01OVV004)" . "RIV/00216305:26310/13:PU105270!RIV14-MK0-26310___" . "Kr\u010Dma, Franti\u0161ek" .