. "RIV/00216305:26310/12:PU99331" . "S" . "26310" . . "Kr\u010Dma, Franti\u0161ek" . . "[D147AAD18A6E]" . . . . "5"^^ . . "This work deals with the diaphragm discharge generated in water solutions containing Na2SO4 as a supporting electrolyte. The solution conductivity was varied in the range of 270-750 microS/cm. The batch plasma reactor with volume of 100 ml was divided into two electrode spaces by the Shapal-M ceramics dielectric barrier with a pin-hole (diameter of 0.6 mm). Three variable barrier thicknesses (0.3; 0.7 and 1.5 mm) and non-pulsed DC voltage up to 2 kV were used for the discharge creation. Each of the current-voltage characteristic can be divided into three parts: electrolysis, bubble formation and discharge operation. The experimental results showed that the discharge ignition moment in the pin-hole was significantly dependent on the dielectric diaphragm thickness. Breakdown voltage increases with the increase of the dielectric barrier thickness." . "RIV/00216305:26310/12:PU99331!RIV13-MSM-26310___" . . "This work deals with the diaphragm discharge generated in water solutions containing Na2SO4 as a supporting electrolyte. The solution conductivity was varied in the range of 270-750 microS/cm. The batch plasma reactor with volume of 100 ml was divided into two electrode spaces by the Shapal-M ceramics dielectric barrier with a pin-hole (diameter of 0.6 mm). Three variable barrier thicknesses (0.3; 0.7 and 1.5 mm) and non-pulsed DC voltage up to 2 kV were used for the discharge creation. Each of the current-voltage characteristic can be divided into three parts: electrolysis, bubble formation and discharge operation. The experimental results showed that the discharge ignition moment in the pin-hole was significantly dependent on the dielectric diaphragm thickness. Breakdown voltage increases with the increase of the dielectric barrier thickness."@en . . . "158734" . "Pin-Hole Discharge Creation in Na2SO4 Water Solutions" . "Hlochov\u00E1, Lenka" . . . "Pin-Hole Discharge Creation in Na2SO4 Water Solutions"@en . "Pin-Hole Discharge Creation in Na2SO4 Water Solutions" . . "Koz\u00E1kov\u00E1, Zdenka" . "Pin-Hole Discharge Creation in Na2SO4 Water Solutions"@en . "Hlavat\u00E1, Lucie" . . "4"^^ . . . . "Diaphragm discharge, current-voltage characteristics, discharge breakdown"@en . .