. "Fe-Zn Intermetallic coatings were prepared. ULC steel (20 ppm C) was used as the substrate. Coating were prepared in the laboratory simulator Rhesca at well defined conditions: dipping time, duration and temperature of annealing. Metallography micrographs of the coating were obtained and the phase composition was observed. The top layer formed by pure zinc was then removed by etching, coatings were moved onto an acrylate mounting resin and such samples were thinned to aprox. 100 um. Transmission M\u00F6ssbauer spectra with high signal-to-noise ratio were measured. Spectra were fitted using the least square method. The effect of galvanneling conditions on isomer shift, quadrupole splitting and relative area of individual sites of iron in the intermetallic phases was evaluated. Based on the observed tendencies, hypothesis about phase transformations during galvanizing were expressed. Results were compared to previous ones obtained by scattering measurements of commercial coatings."@en . . "Czechoslovak Journal of Physics" . . "26310" . "Structure of intermetallic phases in Al-free galvannealed zinc coatings" . "Mossbauer spectroscopy, zinc coating"@en . "Fe-Zn Intermetallic coatings were prepared. ULC steel (20 ppm C) was used as the substrate. Coating were prepared in the laboratory simulator Rhesca at well defined conditions: dipping time, duration and temperature of annealing. Metallography micrographs of the coating were obtained and the phase composition was observed. The top layer formed by pure zinc was then removed by etching, coatings were moved onto an acrylate mounting resin and such samples were thinned to aprox. 100 um. Transmission M\u00F6ssbauer spectra with high signal-to-noise ratio were measured. Spectra were fitted using the least square method. The effect of galvanneling conditions on isomer shift, quadrupole splitting and relative area of individual sites of iron in the intermetallic phases was evaluated. Based on the observed tendencies, hypothesis about phase transformations during galvanizing were expressed. Results were compared to previous ones obtained by scattering measurements of commercial coatings." . "544985" . . "RIV/00216305:26310/05:PU75139!RIV10-MSM-26310___" . "Structure of intermetallic phases in Al-free galvannealed zinc coatings"@en . "[F7DC477AC85F]" . "CZ - \u010Cesk\u00E1 republika" . . . . . "Structure of intermetallic phases in Al-free galvannealed zinc coatings" . . "Schneeweiss, Old\u0159ich" . "2002(55)" . . "RIV/00216305:26310/05:PU75139" . "Zmrzl\u00FD, Martin" . "2"^^ . "12"^^ . "4"^^ . "7" . . . . "Fiala, Jaroslav" . . . "Structure of intermetallic phases in Al-free galvannealed zinc coatings"@en . "0011-4626" . . "Houbaert, Yvan" . "Z(AV0Z20410507), Z(MSM0021630501)" .