"Perovskite-type Orthoferrite Pigments with General Formula Lu0.98Ca0.02Fe1-xMxO3" . "RIV/00216275:25310/13:39896190!RIV14-MSM-25310___" . . . "The color properties of perovskite pigments with general formula Ln0,98Ca0,02FeO2,99, where Ln = La, Gd, Lu, Tm, Yb and Ho were examined. The pigment Lu0,98Ca0,02FeO2,99 prepared from FeOOH was chosen as the color most interesting This pigment was prepared at the different firing temperature and was subjected to X-ray diffraction analysis and was examined of influence of mineralizers (Na2SiF6, Na3AlF6, NaF, LiF and AlF3) on this color properties. Next the pigments of type Lu0,98Ca0,02Fe1-xMxO3??, where M = Zr, Sn, Bi, Sb, Zn, Co and Ti, x=0.1; 0.3 and 0.5 were prepared and their color properties were examined. The pigments were prepared by dry way with followed calcinations at the firing temperature 900 \u00B0C for two hours. The color properties were objectively evaluated using the spectrophotometer ColorQuerst XE. The particle size of pigments were measured by laser Mastersizer 2000 MU. Next the influence of added of mineralizer LiF on the color properties of these pigments. The pigments in the presence of LiF were subjected X-ray diffraction analysis also."@en . . "Perovskite-type Orthoferrite Pigments with General Formula Lu0.98Ca0.02Fe1-xMxO3"@en . "25310" . "95846" . "2013-04-08+02:00"^^ . "[6D1658532B7C]" . . "The color properties of perovskite pigments with general formula Ln0,98Ca0,02FeO2,99, where Ln = La, Gd, Lu, Tm, Yb and Ho were examined. The pigment Lu0,98Ca0,02FeO2,99 prepared from FeOOH was chosen as the color most interesting This pigment was prepared at the different firing temperature and was subjected to X-ray diffraction analysis and was examined of influence of mineralizers (Na2SiF6, Na3AlF6, NaF, LiF and AlF3) on this color properties. Next the pigments of type Lu0,98Ca0,02Fe1-xMxO3??, where M = Zr, Sn, Bi, Sb, Zn, Co and Ti, x=0.1; 0.3 and 0.5 were prepared and their color properties were examined. The pigments were prepared by dry way with followed calcinations at the firing temperature 900 \u00B0C for two hours. The color properties were objectively evaluated using the spectrophotometer ColorQuerst XE. The particle size of pigments were measured by laser Mastersizer 2000 MU. Next the influence of added of mineralizer LiF on the color properties of these pigments. The pigments in the presence of LiF were subjected X-ray diffraction analysis also." . . . . . "Vontor\u010D\u00EDkov\u00E1, Mark\u00E9ta" . "Sborn\u00EDk p\u0159\u00EDsp\u011Bvk\u016F 1st International Conference on Chemical Technology 2013" . "S" . "\u0160ulcov\u00E1, Petra" . "Color; Chroma; Lanthanide; Mineralizer; Pigment"@en . "978-80-86238-37-1" . "Dohnalov\u00E1, \u017Daneta" . . . . . "RIV/00216275:25310/13:39896190" . "3"^^ . . "Mikulov" . "Perovskite-type Orthoferrite Pigments with General Formula Lu0.98Ca0.02Fe1-xMxO3" . "Praha" . . "4"^^ . "3"^^ . . . . . "Perovskite-type Orthoferrite Pigments with General Formula Lu0.98Ca0.02Fe1-xMxO3"@en . . . "\u010Cesk\u00E1 spole\u010Dnost pr\u016Fmyslov\u00E9 chemie" .