. "3"^^ . "*V r\u00E1mci smluvn\u00EDho v\u00FDzkumu byly provedeny predikce f\u00E1zov\u00FDch diagram\u016F n\u00EDzkolegovan\u00FDch ocel\u00ED Fe-C-Si-Mn, Fe-C-Si a Fe-C-Al programy Thermocalc a Factsage ve kter\u00FDch je implementov\u00E1na metoda CALPHAD. Na z\u00E1klad\u011B dodan\u00FDm experiment\u00E1ln\u00EDch v\u00FDsledk\u016F termick\u00E9 anal\u00FDzy byl proveden assessment relevantn\u00EDch termodynamick\u00FDch parametr\u016F. Datab\u00E1ze SGTE2011 byla roz\u0161\u00ED\u0159ena o nov\u011B optimalizovan\u00E9 parametry. Zpr\u00E1va je ulo\u017Eena v Repozit\u00E1\u0159i zam\u011Bstnaneck\u00FDch d\u011Bl MU." . . . "Assessment of phase diagrams of low-alloy steels"@en . . . "Assessment of phase diagrams of low-alloy steels"@en . "62246" . "2"^^ . "Zoba\u010D, Ond\u0159ej" . "Voestalpine Stahl" . "2"^^ . . "14740" . "Assessment f\u00E1zov\u00FDch diagram\u016F n\u00EDzkolegovan\u00FDch ocel\u00ED"@cs . "Voestalpine; steel; phase diagrams; CALPHAD"@en . . . "Neuveden" . "RIV/00216224:14740/13:00073072" . "*V r\u00E1mci smluvn\u00EDho v\u00FDzkumu byly provedeny predikce f\u00E1zov\u00FDch diagram\u016F n\u00EDzkolegovan\u00FDch ocel\u00ED Fe-C-Si-Mn, Fe-C-Si a Fe-C-Al programy Thermocalc a Factsage ve kter\u00FDch je implementov\u00E1na metoda CALPHAD. Na z\u00E1klad\u011B dodan\u00FDm experiment\u00E1ln\u00EDch v\u00FDsledk\u016F termick\u00E9 anal\u00FDzy byl proveden assessment relevantn\u00EDch termodynamick\u00FDch parametr\u016F. Datab\u00E1ze SGTE2011 byla roz\u0161\u00ED\u0159ena o nov\u011B optimalizovan\u00E9 parametry. Zpr\u00E1va je ulo\u017Eena v Repozit\u00E1\u0159i zam\u011Bstnaneck\u00FDch d\u011Bl MU."@cs . . . "RIV/00216224:14740/13:00073072!RIV14-MSM-14740___" . "Sopou\u0161ek, Ji\u0159\u00ED" . "Assessment f\u00E1zov\u00FDch diagram\u016F n\u00EDzkolegovan\u00FDch ocel\u00ED" . . "Assessment f\u00E1zov\u00FDch diagram\u016F n\u00EDzkolegovan\u00FDch ocel\u00ED"@cs . . "Masarykova univerzita, Brno" . . "[1632C73A0E35]" . "N" . "*In the context of contract research were carried prediction of phase diagrams of low-alloy steels Fe-C-Si-Mn, Fe-C-Si and Fe-C-Al Thermocalc programs and Factsage where it is implemented CALPHAD method. Based on the supplied experimental results of thermal analysis was carried out assessment of the relevant thermodynamic parameters. SGTE2011 database was expanded to include newly optimized parameters. The report is stored in Repository of MU."@en . "Assessment f\u00E1zov\u00FDch diagram\u016F n\u00EDzkolegovan\u00FDch ocel\u00ED" . . . . .