"3"^^ . "Nominally undoped, hydrothermally grown ZnO single crystals have been investigated before and after exposure to remote H plasma. Structural characterizations have been made by various positron annihilation spectroscopies (continuous and pulsed slow positron beams, conventional lifetime). The content of bound hydrogen (H-b) before and after the remote H plasma treatment at the polished side of the crystals was determined at depths of 100 and 600 nm, respectively, using nuclear reaction analysis. At a depth of 100 nm, H-b increased from (11.8+-2.5) to (48.7+-7.6)x10^19 cm^-3 after remote H plasma treatment, whereas at 600 nm no change in H-b was observed." . . . "RIV/00216208:11320/10:10064255" . . . . . . . . . "11320" . "11" . "Sperr, Peter" . "Grambole, Dieter" . "Physica Status Solidi (A) Applications and Materials" . "Anwand, Wolfgang" . . "10"^^ . "000284055700001" . "Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies"@en . "1862-6300" . "Brauer, Gerhard" . "P(KJB101120906), P(OC 165), Z(MSM0021620834)" . . . "RIV/00216208:11320/10:10064255!RIV11-MSM-11320___" . . "11"^^ . . "207" . "DE - Spolkov\u00E1 republika N\u011Bmecko" . "Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies" . "Skorupa, Wolfgang" . . "Cowan, Thomas E." . "NRA; positron annihilation; ZnO single crystals; H-plasma doping"@en . "[D60A63616BE9]" . . "Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies"@en . "Kuriplach, Jan" . "Egger, Werner" . . "Structural characterization of H plasma-doped ZnO single crystals by positron annihilation spectroscopies" . . . . "\u010C\u00ED\u017Eek, Jakub" . "Nominally undoped, hydrothermally grown ZnO single crystals have been investigated before and after exposure to remote H plasma. Structural characterizations have been made by various positron annihilation spectroscopies (continuous and pulsed slow positron beams, conventional lifetime). The content of bound hydrogen (H-b) before and after the remote H plasma treatment at the polished side of the crystals was determined at depths of 100 and 600 nm, respectively, using nuclear reaction analysis. At a depth of 100 nm, H-b increased from (11.8+-2.5) to (48.7+-7.6)x10^19 cm^-3 after remote H plasma treatment, whereas at 600 nm no change in H-b was observed."@en . "Proch\u00E1zka, Ivan" . "290430" .