| - In chemical and power engineering, tube systems are exposed to complex mechanical loading, high temperature, corrosion environment, etc. Long-time influence and interaction of severe conditions can result in the degradation of crucial properties of structural materials. Experimental research was aimed to the study of fatigue properties of three chrome-molybdenum steels: P91, ČSN 15 313 and N10 (21CrVMoW12). CT-specimens were cut out from thick-walled tubes. Materials of the tubes were tested in two different stages - original (without degradation), and degraded. Besides the material state and stress ratio, also orientation and location of specimens in the tube wall were under study, but the influence of these factors on fatigue crack growth was negligible. Fractographic analysis of the fatigued specimens was carried out.
- In chemical and power engineering, tube systems are exposed to complex mechanical loading, high temperature, corrosion environment, etc. Long-time influence and interaction of severe conditions can result in the degradation of crucial properties of structural materials. Experimental research was aimed to the study of fatigue properties of three chrome-molybdenum steels: P91, ČSN 15 313 and N10 (21CrVMoW12). CT-specimens were cut out from thick-walled tubes. Materials of the tubes were tested in two different stages - original (without degradation), and degraded. Besides the material state and stress ratio, also orientation and location of specimens in the tube wall were under study, but the influence of these factors on fatigue crack growth was negligible. Fractographic analysis of the fatigued specimens was carried out. (en)
- Potrubní systémy jsou v chemickém průmyslu a v energetice vystaveny kombinovaným účinkům složitého mechanického namáhání, vysoké teploty, korozi apod. Dlouhodobým vlivem interakce uvedených faktorů může dojít k degradaci rozhodujících vlastností konstrukčních materiálů. Experimentální výzkum byl zaměřen na studium únavových vlastností tří chrom-molybdenových ocelí: P91, ČSN 15 313 and N10 (21CrVMoW12). Zkušební tělesa typu CT byla odebrána z tlustostěnných trubek. Materiál trubek byl ve dvou odlišných stavech - původním a degradovaném. Kromě stavu materiálu a parametru asymetrie cyklu byla dále sledována orientace a poloha tělesa ve stěně trubky, ale vliv těchto faktorů byl zanedbatelný. Lomové plochy těles, porušených při únavových zkouškách, byly podrobeny fraktografické analýze. (cs)
|
| Title
| - Influence of High Temperature Degradation on Fatigue Crack Growth in Cr-Mo Tube Steels
- Vliv vysokoteplotní degradace na šíření únavových trhlin v Cr-Mo ocelích používaných na výrobu potrubí (cs)
- Influence of High Temperature Degradation on Fatigue Crack Growth in Cr-Mo Tube Steels (en)
|
| skos:prefLabel
| - Influence of High Temperature Degradation on Fatigue Crack Growth in Cr-Mo Tube Steels
- Vliv vysokoteplotní degradace na šíření únavových trhlin v Cr-Mo ocelích používaných na výrobu potrubí (cs)
- Influence of High Temperature Degradation on Fatigue Crack Growth in Cr-Mo Tube Steels (en)
|
| skos:notation
| - RIV/68407700:21340/05:04113296!RIV06-MSM-21340___
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21340/05:04113296
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Cr-Mo steels; chemical engineering; crack growth rate; degradation; fatigue; high temperature; power industry; regeneration; stress ratio; tube systems (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...v/mistoKonaniAkce
| |
| http://linked.open...i/riv/mistoVydani
| |
| http://linked.open...i/riv/nazevZdroje
| - Proceedings of Workshop 2005 - Part A,B
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...iv/tvurceVysledku
| - Siegl, Jan
- Kunz, Jiří
- Kopřiva, Petr
- Kudrman, J.
|
| http://linked.open...vavai/riv/typAkce
| |
| http://linked.open.../riv/zahajeniAkce
| |
| http://linked.open...n/vavai/riv/zamer
| |
| number of pages
| |
| http://purl.org/ne...btex#hasPublisher
| - České vysoké učení technické v Praze
|
| https://schema.org/isbn
| |
| http://localhost/t...ganizacniJednotka
| |
| is http://linked.open...avai/riv/vysledek
of | |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)