| - The static and fatigue behaviour of hot rolled Fe-31.5Al-3.5Cr (at%) with addition of zirconium and carbon was studied at different temperatures. The tensile deformation tests were carried out at temperatures ranging from 20 to 600°C. The fatigue crack growth rate (v-deltaK ) curves were measured at 20, 300 and 500°C. The best fatigue crack growth resistance was reached at 300°C, while at 500°C the crack growth rate was the highest and the fatigue life the shortest. The predominant fatigue fracture mechanism is transgranular cleavage. However, a number of other micromorphologic features corresponding to various fracture mechanisms were observed: transgranular quasi-cleavage facets, ductile fatigue striations and brittle striations.
- The static and fatigue behaviour of hot rolled Fe-31.5Al-3.5Cr (at%) with addition of zirconium and carbon was studied at different temperatures. The tensile deformation tests were carried out at temperatures ranging from 20 to 600°C. The fatigue crack growth rate (v-deltaK ) curves were measured at 20, 300 and 500°C. The best fatigue crack growth resistance was reached at 300°C, while at 500°C the crack growth rate was the highest and the fatigue life the shortest. The predominant fatigue fracture mechanism is transgranular cleavage. However, a number of other micromorphologic features corresponding to various fracture mechanisms were observed: transgranular quasi-cleavage facets, ductile fatigue striations and brittle striations. (en)
- Statické a dynamické mechanické vlastnosti intermetalické slitiny Fe-31,5Al-3,5Cr (at%) legované zirkonem a uhlíkem a válcované za tepla byly studovány při různých teplotách. Tahové zkoušky byly provedeny v rozmezí teplot 20 až 600°C. Závislosti rychlosti šíření únavové trhliny na rozkmitu faktoru intenzity napětí (v-deltaK ) byly proměřeny při teplotách 20, 300 a 500°C. Nejvyšší únavová odolnost byla dosažena při zkouškách za teploty 300°C, zatímco při testech při 500°C byla rychlost šíření únavové trhliny nejvyšší a únavový život testovaných vzorků nejkratší. Převládajícím typem únavového porušování byl transkrystalický štěpný lom. Byly pozorovány i jiné mikromorfologické znaky odpovídajícím různým mechanismům porušování (transkrystalické kvazi-štěpné fasety, tvárné a štěpné striace). Za vysokých teplot obsahoval lomový povrch v oblasti statického dolomení známky plastické deformace, které se rostoucí teplotou vyskytovaly častěji (cs)
|
Title
| - Fracture behaviour of Fe3Al alloy with additions of Zr and C at different temperatures
- Lomové chování slitiny Fe3Al s přísadou Zr a C za různých teplot (cs)
- Fracture behaviour of Fe3Al alloy with additions of Zr and C at different temperatures (en)
|
skos:prefLabel
| - Fracture behaviour of Fe3Al alloy with additions of Zr and C at different temperatures
- Lomové chování slitiny Fe3Al s přísadou Zr a C za různých teplot (cs)
- Fracture behaviour of Fe3Al alloy with additions of Zr and C at different temperatures (en)
|
skos:notation
| - RIV/68407700:21340/05:04108232!RIV06-GA0-21340___
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GA106/02/0687), Z(MSM6840770021)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21340/05:04108232
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - fatigue crack growth; fractography; fracture micromechanisms; iron aluminides (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Haušild, Petr
- Karlík, Miroslav
- Prahl, Jakub
- Crenn, J.-F.
|
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://localhost/t...ganizacniJednotka
| |
is http://linked.open...avai/riv/vysledek
of | |