| - Ti-C:H coatings with different carbon content for biomedical applications were deposited by PECVD. Ti was varied by magnetron sputtering a Ti-target with different power in a dc discharge regime having Ar in the atmosphere. The tribological properties were studied using a pin-on-disc CSM Tribometer in order to ensure stable tribological properties of the whole Ti-C:H/DLC system for any case of top layer failure. The sliding tests were carried out at room temperature in room environment with relative air humidity 40+-5%, in 0.9% NaCl water solution (physiological solution, PS) and in 10% fetal bovine serum (FBS) dissolved in Ringer's saline solution using 440C steel balls with a diameter of 8 mm. The Ti-rich coatings exhibited poor wear resistance, while the best tribological properties were achieved for TiC/a-C:H coatings deposited with the highest C2H2 flows.
- Ti-C:H coatings with different carbon content for biomedical applications were deposited by PECVD. Ti was varied by magnetron sputtering a Ti-target with different power in a dc discharge regime having Ar in the atmosphere. The tribological properties were studied using a pin-on-disc CSM Tribometer in order to ensure stable tribological properties of the whole Ti-C:H/DLC system for any case of top layer failure. The sliding tests were carried out at room temperature in room environment with relative air humidity 40+-5%, in 0.9% NaCl water solution (physiological solution, PS) and in 10% fetal bovine serum (FBS) dissolved in Ringer's saline solution using 440C steel balls with a diameter of 8 mm. The Ti-rich coatings exhibited poor wear resistance, while the best tribological properties were achieved for TiC/a-C:H coatings deposited with the highest C2H2 flows. (en)
|
Title
| - Structure and Tribology of Biocompatible Ti-C:H Coatings
- Structure and Tribology of Biocompatible Ti-C:H Coatings (en)
|
skos:prefLabel
| - Structure and Tribology of Biocompatible Ti-C:H Coatings
- Structure and Tribology of Biocompatible Ti-C:H Coatings (en)
|
skos:notation
| - RIV/68407700:21220/07:00142349!RIV12-MSM-21220___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(2A-1TP1/031), P(KJB201240701), P(OE 205)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21220/07:00142349
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Ti-C:H coatings; fetal bovine serum; physiological solution; tribology (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Cavaleiro, A.
- Polcar, Tomáš
- Vítů, Tomáš
- Cvrček, L.
- Novák, Rudolf
- Vyskočil, J.
- Macák, J.
|
http://localhost/t...ganizacniJednotka
| |