| - The fatigue crack growth rate in the Eurofer 97 steel was measured by two different methodologies. Small crack growth data were obtained using cylindrical specimens with a shallow notch. No artificial crack starters were used. The growth of semicircular cracks of length between 10 – 2000 m were measured in symmetrical tension-compression cycling with constant strain amplitude (R = -1). Long crack data were measured using standard CT specimen and ASTM methodology in stress control with R = 0.1. The growth of fatigue cracks with length in the range of 10 – 30 mm was determined. It is shown that the crack growth rate of both types of cracks are in a very good agreement if J-integral rep-resentation is used and reasonable assumptions of the crack closure effects are taken into account. (en)
- Rychlost růstu únavových trhlin v oceli Eurofer 97 byla měřena dvěma odlišnými metodologiemi. Data pro malé trhliny byly získány na válcových vzorcích s mělkým vrubem. Růst polokruhových trhlin o délce mezi 10-2000 mikrometry byly měřeny při symetrickém cyklu tah-tlak s konstantní amplitudou deformace. Data k šíření dlouhých trhlin (10 – 30 mm) byla získána na CT vzorcích pomocí procedury popsané v ASTM normě při řízení napětí s R = 0.1. Bylo ukázáno, že rychlosti šíření obou typů trhlin jsou ve velmi dobrém souhlasu, pokud je použito srovnání pomocí J-integrálu a jsou uplatněny běžně přijímané předpoklady o efektu zavírání trhliny.
- Rychlost růstu únavových trhlin v oceli Eurofer 97 byla měřena dvěma odlišnými metodologiemi. Data pro malé trhliny byly získány na válcových vzorcích s mělkým vrubem. Růst polokruhových trhlin o délce mezi 10-2000 mikrometry byly měřeny při symetrickém cyklu tah-tlak s konstantní amplitudou deformace. Data k šíření dlouhých trhlin (10 – 30 mm) byla získána na CT vzorcích pomocí procedury popsané v ASTM normě při řízení napětí s R = 0.1. Bylo ukázáno, že rychlosti šíření obou typů trhlin jsou ve velmi dobrém souhlasu, pokud je použito srovnání pomocí J-integrálu a jsou uplatněny běžně přijímané předpoklady o efektu zavírání trhliny. (cs)
|
Title
| - Kinetika růstu únavových trhlin v oceli Eurofer 97
- Kinetics of fatigue crack growth in Eurofer 97 steel (en)
- Kinetika růstu únavových trhlin v oceli Eurofer 97 (cs)
|
skos:prefLabel
| - Kinetika růstu únavových trhlin v oceli Eurofer 97
- Kinetics of fatigue crack growth in Eurofer 97 steel (en)
- Kinetika růstu únavových trhlin v oceli Eurofer 97 (cs)
|
skos:notation
| - RIV/68081723:_____/10:00353536!RIV11-GA0-68081723
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GA101/09/0867), P(GA106/09/1954), Z(AV0Z20410507)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68081723:_____/10:00353536
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - fatigue crack growth; ferritic martensitic steel; low cycle fatigue (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Engineering Mechanics 2010
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Hutař, Pavel
- Kruml, Tomáš
- Náhlík, Luboš
- Polák, Jaroslav
- Seitl, Stanislav
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
http://linked.open...n/vavai/riv/zamer
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| - Ústav termomechaniky AV ČR
|
https://schema.org/isbn
| |
is http://linked.open...avai/riv/vysledek
of | |