About: Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo

Facets (new session)
Description
Metadata
Settings
- owl:sameAs
- Inference Rule:

About: Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo Goto Sponge NotDistinct Permalink

An Entity of Type : http://linked.opendata.cz/ontology/domain/vavai/Vysledek, within Data Space : linked.opendata.cz associated with source document(s)

Attributes	Values
rdf:type	skos:Concept http://linked.opendata.cz/ontology/domain/vavai/Vysledek
Description	The paper evaluates resistance of the welded joint made of supermartensitic steel 13Cr6Ni2.5Mo to sulfide stress cracking (SSC). None of the tested samples withstood the required values of loading, failure occurred already at very short time intervals. Unsatisfactory resistance can be attributed to high values of mechanical properties of material, which did not sufficiently decrease by tempering, and also to occurrence of undesirable δ-ferrite in structure. In spite of that it was revealed that the welded joint brought even further reduction of resistance to SSC, because the fracture occurred in the samples with welded joint primarily in the weld metal (WM) or in heat affected zone (HAZ) and not in the basic material. The paper evaluates resistance of the welded joint made of supermartensitic steel 13Cr6Ni2.5Mo to sulfide stress cracking (SSC). None of the tested samples withstood the required values of loading, failure occurred already at very short time intervals. Unsatisfactory resistance can be attributed to high values of mechanical properties of material, which did not sufficiently decrease by tempering, and also to occurrence of undesirable δ-ferrite in structure. In spite of that it was revealed that the welded joint brought even further reduction of resistance to SSC, because the fracture occurred in the samples with welded joint primarily in the weld metal (WM) or in heat affected zone (HAZ) and not in the basic material. (en)
Title	Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo (en)
skos:prefLabel	Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo (en)
skos:notation	RIV/61989100:27360/08:00019503!RIV10-MSM-27360___
http://linked.open...avai/riv/aktivita	Z
http://linked.open...avai/riv/aktivity	Z(MSM6198910015)
http://linked.open...vai/riv/dodaniDat	2010
http://linked.open...aciTvurceVysledku	Hlaváč, Libor Sojka, Jaroslav Váňová, Petra Jonšta, Petr
http://linked.open.../riv/druhVysledku	D - Článek ve sborníku
http://linked.open...iv/duvernostUdaju	S - Úplné a pravdivé údaje nepodléhající ochraně podle zvláštních právních předpisů
http://linked.open...titaPredkladatele	Vysoká škola báňská - Technická univerzita Ostrava / Fakulta metalurgie a materiálového inženýrství
http://linked.open...dnocenehoVysledku	398333
http://linked.open...ai/riv/idVysledku	RIV/61989100:27360/08:00019503
http://linked.open...riv/jazykVysledku	eng - angličtina
http://linked.open.../riv/klicovaSlova	sulphide stress cracking; welded joint; microstructure; heat affected zone (HAZ) (en)
http://linked.open.../riv/klicoveSlovo	welded joint sulphide stress cracking microstructure heat affected zone (HAZ)
http://linked.open...ontrolniKodProRIV	[35893F9A5344]
http://linked.open...v/mistoKonaniAkce	Jarnoltówek
http://linked.open...i/riv/mistoVydani	Opole
http://linked.open...i/riv/nazevZdroje	Zeszyty Naukowe, Mechanika
http://linked.open...in/vavai/riv/obor	JG
http://linked.open...ichTvurcuVysledku	4 (xsd:int)
http://linked.open...cetTvurcuVysledku	6 (xsd:int)
http://linked.open...UplatneniVysledku	2008
http://linked.open...iv/tvurceVysledku	Jonšta, Petr Sojka, Jaroslav Hlaváč, Libor Váňová, Petra Gembalová, Lucie Kaličinský, Jiří
http://linked.open...vavai/riv/typAkce	EUR - Evropská
http://linked.open.../riv/zahajeniAkce	2008-10-22 (xsd:date)
http://linked.open...n/vavai/riv/zamer	Structural potentiality and properties of intensively formed materials
issn	1429-6055
number of pages	8 (xsd:int)
http://purl.org/ne...btex#hasPublisher	Politechnika Opolska
http://localhost/t...ganizacniJednotka	27360
is http://linked.open...avai/riv/vysledek of	Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo

Faceted Search & Find service v1.16.118 as of Jun 21 2024

Alternative Linked Data Documents: ODE Content Formats:

RDF

ODATA

Microdata

About

OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 58 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software