| - The paper is focused on evaluation of two heats of duplex stainless steel, containing 22 % of Cr and 5% of Ni, to sulphide stress cracking (SSC) with regard to their characteristics of surface roughness. Steels were tested in initial state after rolling and solution annealing and after laboratory annealings, the aim of which was to provoke phase σ formation. Annealing at temperatures 675 0C and 800 0C resulted in phase σ precipitation at the ferrite/austenite interface. SSC tests were carried out in accordance to NACE TM 0177-03. It seems, resistance of duplex steels to SSC can be also affected with occurrence of ?micro-notches? on test parts of tensile test specimens. (en)
- Příspěvek se zabývá hodnocením dvou taveb duplexní oceli 2205 vůči sulfidickému praskání pod napětím s přihlédnutím k jejich charakteristikám drsnosti povrchu. Oceli byly testovány ve výchozím stavu po válcování a rozpouštěcím žíhání a ve stavu po laboratorním žíhání režimy 675 0C/5 h/vzduch a 800 0C/5 h/vzduch. Cílem laboratorního žíhání byla precipitace fáze σ na fozhraní ferit/austenit. Testování odolnosti ocelí vůči SSC proběhlo plně v souladu s předpisem NACE TM 0177-03, zkušební metodou A. Zdá se, že odolnost duplexních ocelí vůči SSC může být, kromě jiného, ovlivněna přítomnosti ?mikrovrubů? na zkušebních částech vzorků.
- Příspěvek se zabývá hodnocením dvou taveb duplexní oceli 2205 vůči sulfidickému praskání pod napětím s přihlédnutím k jejich charakteristikám drsnosti povrchu. Oceli byly testovány ve výchozím stavu po válcování a rozpouštěcím žíhání a ve stavu po laboratorním žíhání režimy 675 0C/5 h/vzduch a 800 0C/5 h/vzduch. Cílem laboratorního žíhání byla precipitace fáze σ na fozhraní ferit/austenit. Testování odolnosti ocelí vůči SSC proběhlo plně v souladu s předpisem NACE TM 0177-03, zkušební metodou A. Zdá se, že odolnost duplexních ocelí vůči SSC může být, kromě jiného, ovlivněna přítomnosti ?mikrovrubů? na zkušebních částech vzorků. (cs)
|
Title
| - VLIV DRSNOSTI POVRCHU NA ODOLNOST DUPLEXNÍCH OCELÍ VŮČI SULFIDICKÉMU PRASKÁNÍ POD NAPĚTÍM
- VLIV DRSNOSTI POVRCHU NA ODOLNOST DUPLEXNÍCH OCELÍ VŮČI SULFIDICKÉMU PRASKÁNÍ POD NAPĚTÍM (cs)
- INFLUENCE OF SURFACE ROUGHNESS ON RESISTANCE OF DUPLEX STEELS TO SULPHIDE STRESS CRACKING (en)
|
skos:prefLabel
| - VLIV DRSNOSTI POVRCHU NA ODOLNOST DUPLEXNÍCH OCELÍ VŮČI SULFIDICKÉMU PRASKÁNÍ POD NAPĚTÍM
- VLIV DRSNOSTI POVRCHU NA ODOLNOST DUPLEXNÍCH OCELÍ VŮČI SULFIDICKÉMU PRASKÁNÍ POD NAPĚTÍM (cs)
- INFLUENCE OF SURFACE ROUGHNESS ON RESISTANCE OF DUPLEX STEELS TO SULPHIDE STRESS CRACKING (en)
|
skos:notation
| - RIV/61989100:27360/07:00016264!RIV09-MSM-27360___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61989100:27360/07:00016264
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - duplex steel; phase sigma; roughness; sulphide stress cracking (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Jonšta, Petr
- Sojka, Jaroslav
- Váňová, Petra
- Kubečka, Petr
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| - Žilinská univerzita v Žiline. Strojnícka fakulta
|
http://localhost/t...ganizacniJednotka
| |
is http://linked.open...avai/riv/vysledek
of | |