About: Drop Evaporation Test for stress corrosion cracking study

Facets (new session)
Description
Metadata
Settings
- owl:sameAs
- Inference Rule:

About: Drop Evaporation Test for stress corrosion cracking study Goto Sponge NotDistinct Permalink

An Entity of Type : http://linked.opendata.cz/ontology/domain/vavai/Vysledek, within Data Space : linked.opendata.cz associated with source document(s)

Attributes	Values
rdf:type	skos:Concept http://linked.opendata.cz/ontology/domain/vavai/Vysledek
Description	The drop evaporation test (DET) was developed for study of stainless steels resistance to stress corrosion cracking (SCC) at elevated temperatures 120 - 300 °C under constant external load and dropping of diluted sodium chloride water solution. The resistance to SCC is determined according to time to fracture - tensile stress relations and conventional threshold stress. The alloy (steel) NiCrWTiAl 35-15-5 after thermal hardening and long-time service exposition was tested under DET conditions and corrosion cracks were evaluated by metallography and fractography. The microscopic pits and corrosion crack tips coordinates measurement by the travelling microscope method allowed to determine their lengths and rates as function of time and stress intensity factor. These calculated rates were higher when cracks leaving the pits. The resistance to intergranular corrosion was compared by DL-EPR (double loop electrochemical potenciokinetic reactivation) method. The drop evaporation test (DET) was developed for study of stainless steels resistance to stress corrosion cracking (SCC) at elevated temperatures 120 - 300 °C under constant external load and dropping of diluted sodium chloride water solution. The resistance to SCC is determined according to time to fracture - tensile stress relations and conventional threshold stress. The alloy (steel) NiCrWTiAl 35-15-5 after thermal hardening and long-time service exposition was tested under DET conditions and corrosion cracks were evaluated by metallography and fractography. The microscopic pits and corrosion crack tips coordinates measurement by the travelling microscope method allowed to determine their lengths and rates as function of time and stress intensity factor. These calculated rates were higher when cracks leaving the pits. The resistance to intergranular corrosion was compared by DL-EPR (double loop electrochemical potenciokinetic reactivation) method. (en)
Title	Drop Evaporation Test for stress corrosion cracking study Drop Evaporation Test for stress corrosion cracking study (en)
skos:prefLabel	Drop Evaporation Test for stress corrosion cracking study Drop Evaporation Test for stress corrosion cracking study (en)
skos:notation	RIV/61989100:27360/03:00008728!RIV/2004/GA0/273604/N
http://linked.open.../vavai/riv/strany	25-33
http://linked.open...avai/riv/aktivita	P
http://linked.open...avai/riv/aktivity	P(GA106/02/1569)
http://linked.open...vai/riv/dodaniDat	2004
http://linked.open...aciTvurceVysledku	Blahetová, Marie Lasek, Stanislav Číhal, Vladimír
http://linked.open.../riv/druhVysledku	D - Článek ve sborníku
http://linked.open...iv/duvernostUdaju	S - Úplné a pravdivé údaje nepodléhající ochraně podle zvláštních právních předpisů
http://linked.open...titaPredkladatele	Vysoká škola báňská - Technická univerzita Ostrava / Fakulta metalurgie a materiálového inženýrství
http://linked.open...dnocenehoVysledku	604484
http://linked.open...ai/riv/idVysledku	RIV/61989100:27360/03:00008728
http://linked.open...riv/jazykVysledku	eng - angličtina
http://linked.open.../riv/klicovaSlova	Corrosion, Cracking, Testing, Evaporation (en)
http://linked.open.../riv/klicoveSlovo	Testing Evaporation Corrosion Cracking
http://linked.open...ontrolniKodProRIV	[E3C478555370]
http://linked.open...v/mistoKonaniAkce	Terchova
http://linked.open...i/riv/mistoVydani	Budapest
http://linked.open...i/riv/nazevZdroje	The Europ. Cor. Congress EUROCORR 2003
http://linked.open...in/vavai/riv/obor	JG
http://linked.open...ichTvurcuVysledku	3 (xsd:int)
http://linked.open...cetTvurcuVysledku	3 (xsd:int)
http://linked.open...ocetUcastnikuAkce	0 (xsd:int)
http://linked.open...nichUcastnikuAkce	0 (xsd:int)
http://linked.open...vavai/riv/projekt	Study of degradation of stainless materials under salting-out conditions at higher temperatures
http://linked.open...UplatneniVysledku	2003
http://linked.open...iv/tvurceVysledku	Blahetová, Marie Lasek, Stanislav Číhal, Vladimír
http://linked.open...vavai/riv/typAkce	WRD - Světová
http://linked.open.../riv/zahajeniAkce	2003-10-28 (xsd:date)
number of pages	9 (xsd:int)
http://purl.org/ne...btex#hasPublisher	Eurocorr
https://schema.org/isbn	80-81-365
http://localhost/t...ganizacniJednotka	27360

Faceted Search & Find service v1.16.118 as of Jun 21 2024

Alternative Linked Data Documents: ODE Content Formats:

RDF

ODATA

Microdata

About

OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 58 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software