| - Polyaniline (PANI) was prepared by the oxidative polymerization of aniline. The deprotonated product, a PANI base, was carbonized in an inert atmosphere at temperatures up to 800 °C for various times. The mass decreased to 40–50 wt.% at temperatures above 600 °C. The progress of molecular structure during carbonization was followed by infrared and Raman spectroscopies. The carbonization at 650 °C for 1 h is suggested for the optimum conversion of PANI to carbon. The product retained the original globular structure of PANI. The conductivity of the carbonized material was low for carbonizations below 600 °C, <1010 S cm1, and increased to 104 S cm1 after treatment at 800 °C. The content of nitrogen, not, vert, similar10 wt.%, was not affected appreciably by the carbonization.
- Polyaniline (PANI) was prepared by the oxidative polymerization of aniline. The deprotonated product, a PANI base, was carbonized in an inert atmosphere at temperatures up to 800 °C for various times. The mass decreased to 40–50 wt.% at temperatures above 600 °C. The progress of molecular structure during carbonization was followed by infrared and Raman spectroscopies. The carbonization at 650 °C for 1 h is suggested for the optimum conversion of PANI to carbon. The product retained the original globular structure of PANI. The conductivity of the carbonized material was low for carbonizations below 600 °C, <1010 S cm1, and increased to 104 S cm1 after treatment at 800 °C. The content of nitrogen, not, vert, similar10 wt.%, was not affected appreciably by the carbonization. (en)
|
Title
| - The carbonization of granular polyaniline to produce nitrogen-containing carbon
- The carbonization of granular polyaniline to produce nitrogen-containing carbon (en)
|
skos:prefLabel
| - The carbonization of granular polyaniline to produce nitrogen-containing carbon
- The carbonization of granular polyaniline to produce nitrogen-containing carbon (en)
|
skos:notation
| - RIV/61389013:_____/11:00360012!RIV12-AV0-61389013
|
http://linked.open...avai/predkladatel
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GA203/08/0686), P(IAA100500902), P(IAA400500905), Z(AV0Z40500505)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61389013:_____/11:00360012
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - polyaniline; conducting polymer; carbon (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - CH - Švýcarská konfederace
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Exnerová, Milena
- Rozlívková, Zuzana
- Stejskal, Jaroslav
- Trchová, Miroslava
|
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| - 10.1016/j.synthmet.2011.03.034
|
is http://linked.open...avai/riv/vysledek
of | |