We have found that above the phase separation temperature Tc the copolymer solution is almost homogeneous while at temperatures below Tc the solution is microphase separated into a periodic lattice generally with body centered morphology.
We have found that above the phase separation temperature Tc the copolymer solution is almost homogeneous while at temperatures below Tc the solution is microphase separated into a periodic lattice generally with body centered morphology. (en)