| - Sklovitý karbon byl implantován ionty 150 keV Co+, nízkou dávkou 1x10(16) a vysokou dávkou 1x10(16)iontů/cm(2). Byly studovány výsledné strukturální změny. (cs)
- Glassy carbon (GC) was implanted by 150 keV Co+ ions to the doses of 1x10(16) (low dose) and 1x10(17) ions/cm(2) (high dose). The low dose implantation results in GC structure disordering with formation of amorphous carbon (a-C). Analysis of Rutherford backscattering (RBS) and Raman spectra has revealed 15 at.% of sp(3)-bonded C atoms in the a-C structure. The in-pane size of sp(2) clusters was estimated to be 1.1 nm. On the contrary, the high dose ion implantation results in ordering of the a-C structure. Content of the sp(3) atoms in a-C was reduced to about 5% and, respectively, the in-plane sp(2) cluster size was increased up to 2.8 nm. Together with the a-C structure ordering the Raman spectra identifies formation of transpolyacetylene (TPA)-like chains after the high-dose Co+ implantation. In parallel, RBS suggests an enhanced diffusion of the implanted cobalt within the modified carbon layer.
- Glassy carbon (GC) was implanted by 150 keV Co+ ions to the doses of 1x10(16) (low dose) and 1x10(17) ions/cm(2) (high dose). The low dose implantation results in GC structure disordering with formation of amorphous carbon (a-C). Analysis of Rutherford backscattering (RBS) and Raman spectra has revealed 15 at.% of sp(3)-bonded C atoms in the a-C structure. The in-pane size of sp(2) clusters was estimated to be 1.1 nm. On the contrary, the high dose ion implantation results in ordering of the a-C structure. Content of the sp(3) atoms in a-C was reduced to about 5% and, respectively, the in-plane sp(2) cluster size was increased up to 2.8 nm. Together with the a-C structure ordering the Raman spectra identifies formation of transpolyacetylene (TPA)-like chains after the high-dose Co+ implantation. In parallel, RBS suggests an enhanced diffusion of the implanted cobalt within the modified carbon layer. (en)
|
Title
| - Structural phenomena in glassy carbon induced by cobalt ion implantation
- Strukturální jevy ve sklovitém karbonu indukované implantací ionty kobaltu (cs)
- Structural phenomena in glassy carbon induced by cobalt ion implantation (en)
|
skos:prefLabel
| - Structural phenomena in glassy carbon induced by cobalt ion implantation
- Strukturální jevy ve sklovitém karbonu indukované implantací ionty kobaltu (cs)
- Structural phenomena in glassy carbon induced by cobalt ion implantation (en)
|
skos:notation
| - RIV/61389005:_____/08:00323181!RIV09-AV0-61389005
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61389005:_____/08:00323181
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - DIAMOND-LIKE CARBON; AMORPHOUS-CARBON; RAMAN-SCATTERING (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - US - Spojené státy americké
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| - Applied Physics A - Materials Science & Processing
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Lavrentiev, Vasyl
- Vacík, Jiří
- Naramoto, H.
|
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
is http://linked.open...avai/riv/vysledek
of | |