| - The extent of thermal template (tetra-propyl-ammonium: TPA+) removal from a silicalite-1 layer by heating in air was investigated. While a temperature of 330oC was sufficient to eliminate all N-containing template species from the surface region of the layer (i.e., within a depth of 10 nm), their complete elimination from the bulk even at 550oC was not achieved. This was caused by a series of reactions proceeding at high temperatures, involving the products of TPA+ thermal degradation. A substantial amount of C-containing template species remained in the sample even after a thermal treatment at 550oC. A role the SiO2 phase of low organization present in the silicalite-1 layer plays in the retention of the products of thermal degradation has been proposed. Additionally, the stability of TPA+ irradiated by microwaves was examined.
- The extent of thermal template (tetra-propyl-ammonium: TPA+) removal from a silicalite-1 layer by heating in air was investigated. While a temperature of 330oC was sufficient to eliminate all N-containing template species from the surface region of the layer (i.e., within a depth of 10 nm), their complete elimination from the bulk even at 550oC was not achieved. This was caused by a series of reactions proceeding at high temperatures, involving the products of TPA+ thermal degradation. A substantial amount of C-containing template species remained in the sample even after a thermal treatment at 550oC. A role the SiO2 phase of low organization present in the silicalite-1 layer plays in the retention of the products of thermal degradation has been proposed. Additionally, the stability of TPA+ irradiated by microwaves was examined. (en)
- Metodou fotoelektronové spektroskopie (XPS) byl studován rozsah odstranění templátu (tetra-propyl-amonium: TPA+) z povrchu a objemu samonosné vrstvy silikalitu-1 zahříváním v proudu vzduchu ex situ. Informace z povrchu silikalitu 1 byla získána studiem čerstvě syntetizovaných vzorků, objemová informace po jejich rozetření. Z povrchové oblasti (~5 - ~10 nm od povrchu vzorku) byla pro kvantitativní odstranění produktů rozkladu templátu obsahujících dusík dostatečná teplota 330°C. V objemu vzorku nebyl tento efekt dosažen ani při 550°C. Toto je důsledkem řady reakcí spojených s degradací TPA+ probíhajících při vysokých teplotách. Podstatné množství degradačních produktů templátu obsahujících uhlík zůstalo v povrchu i objemu vzorku i po teplotním opracování při teplotě 550°C. Byla navržena představa, jakou úlohu hraje nízkoorganizovaná SiO2 fáze identifikovaná na povrchu silikalitové vrstvy při zádrži produktů tepelné degradace templátu. (cs)
|
| Title
| - Template removal from polycrystalline silicalite-1 self-supporting layer
- Odstraňování templátu ze samonosné vrstvy polykrystalického silikalitu-1 (cs)
- Template removal from polycrystalline silicalite-1 self-supporting layer (en)
|
| skos:prefLabel
| - Template removal from polycrystalline silicalite-1 self-supporting layer
- Odstraňování templátu ze samonosné vrstvy polykrystalického silikalitu-1 (cs)
- Template removal from polycrystalline silicalite-1 self-supporting layer (en)
|
| skos:notation
| - RIV/61388955:_____/05:00000570!RIV06-AV0-61388955
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| - P(GA104/03/0680), P(GA104/04/0963), Z(AV0Z40400503)
|
| http://linked.open...iv/cisloPeriodika
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/61388955:_____/05:00000570
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - microporous materials; surface properties; X-ray photoelectron spectroscopy (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...odStatuVydavatele
| - CN - Čínská lidová republika
|
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...i/riv/nazevZdroje
| - Materials Chemistry and Physics
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...vavai/riv/projekt
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...v/svazekPeriodika
| |
| http://linked.open...iv/tvurceVysledku
| - Novák, Pavel
- Kočiřík, Milan
- Jirka, Ivan
- Zikánová, Arlette
- Čerňanský, Marian
- Weber, Jan
- Pelouchová, Hana
|
| http://linked.open...n/vavai/riv/zamer
| |
| issn
| |
| number of pages
| |
| is http://linked.open...avai/riv/vysledek
of | |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)