About: A positive effect of compressive residual stresses on fatigue strength and damage mechanisms of laser welded structural carbon steel sheets     Goto   Sponge   NotDistinct   Permalink

An Entity of Type : http://linked.opendata.cz/ontology/domain/vavai/Vysledek, within Data Space : linked.opendata.cz associated with source document(s)

AttributesValues
rdf:type
Description
  • The contribution deals with fatigue resistance of laser welded 10 mm thick sheets of a carbon structural S 355 steel. High cycle fatigue tests were performed after optimizing laser welding parameters. Failure occurred mostly in baseic material, so endurance limit of the welds and heat affected zone was higher than that of basic material. The results are discussed on the basis of fractographical analyses, which provided some quite interesting details about crack initiation and growth mechanisms.
  • The contribution deals with fatigue resistance of laser welded 10 mm thick sheets of a carbon structural S 355 steel. High cycle fatigue tests were performed after optimizing laser welding parameters. Failure occurred mostly in baseic material, so endurance limit of the welds and heat affected zone was higher than that of basic material. The results are discussed on the basis of fractographical analyses, which provided some quite interesting details about crack initiation and growth mechanisms. (en)
Title
  • A positive effect of compressive residual stresses on fatigue strength and damage mechanisms of laser welded structural carbon steel sheets
  • A positive effect of compressive residual stresses on fatigue strength and damage mechanisms of laser welded structural carbon steel sheets (en)
skos:prefLabel
  • A positive effect of compressive residual stresses on fatigue strength and damage mechanisms of laser welded structural carbon steel sheets
  • A positive effect of compressive residual stresses on fatigue strength and damage mechanisms of laser welded structural carbon steel sheets (en)
skos:notation
  • RIV/25797000:_____/14:#0000486!RIV15-TA0-25797000
http://linked.open...avai/riv/aktivita
http://linked.open...avai/riv/aktivity
  • P(TA02011004)
http://linked.open...vai/riv/dodaniDat
http://linked.open...aciTvurceVysledku
http://linked.open.../riv/druhVysledku
http://linked.open...iv/duvernostUdaju
http://linked.open...titaPredkladatele
http://linked.open...dnocenehoVysledku
  • 1047
http://linked.open...ai/riv/idVysledku
  • RIV/25797000:_____/14:#0000486
http://linked.open...riv/jazykVysledku
http://linked.open.../riv/klicovaSlova
  • Laser welds; Fatigue strength (en)
http://linked.open.../riv/klicoveSlovo
http://linked.open...i/riv/kodPristupu
http://linked.open...ontrolniKodProRIV
  • [A3D76BAE6C3C]
http://linked.open...i/riv/mistoVydani
  • Institute of Energy and Transport, JRC Petten
http://linked.open...telVyzkumneZpravy
  • IET JRC Petten
http://linked.open...in/vavai/riv/obor
http://linked.open...ichTvurcuVysledku
http://linked.open...cetTvurcuVysledku
http://linked.open...vavai/riv/projekt
http://linked.open...UplatneniVysledku
http://linked.open...iv/tvurceVysledku
  • Černý, Ivo
  • Sís, Jiří
Faceted Search & Find service v1.16.118 as of Jun 21 2024


Alternative Linked Data Documents: ODE     Content Formats:   [cxml] [csv]     RDF   [text] [turtle] [ld+json] [rdf+json] [rdf+xml]     ODATA   [atom+xml] [odata+json]     Microdata   [microdata+json] [html]    About   
This material is Open Knowledge   W3C Semantic Web Technology [RDF Data] Valid XHTML + RDFa
OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 58 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software