| - The drop evaporation test (DET) has been applied to five austenitic and duplex stainless steels containing 15-23% chromium and 6-35% nickel, yielding comparative SCC resistance data. This standard test simulates SCC in aqueous chloride media under conditions involving evaporation at elevated temperatures where the metal is also threatened by potential local concentration changes, precipitation of salts, and deposition of corrosion products. Transgranular corrosion cracks and a ductile shearing fracture mechanism were observed. Corrosion pits acted as stress concentrators and initiators of short cracks propagating at high velocity. The effects of local cooling on the state of stressing of the DET specimens were analyzed using a thermal elasticity model.
- The drop evaporation test (DET) has been applied to five austenitic and duplex stainless steels containing 15-23% chromium and 6-35% nickel, yielding comparative SCC resistance data. This standard test simulates SCC in aqueous chloride media under conditions involving evaporation at elevated temperatures where the metal is also threatened by potential local concentration changes, precipitation of salts, and deposition of corrosion products. Transgranular corrosion cracks and a ductile shearing fracture mechanism were observed. Corrosion pits acted as stress concentrators and initiators of short cracks propagating at high velocity. The effects of local cooling on the state of stressing of the DET specimens were analyzed using a thermal elasticity model. (en)
|
Title
| - INITIATION AND PROPAGATION OF DAMAGE DURING DROP EVAPORATION TEST
- INITIATION AND PROPAGATION OF DAMAGE DURING DROP EVAPORATION TEST (en)
|
skos:prefLabel
| - INITIATION AND PROPAGATION OF DAMAGE DURING DROP EVAPORATION TEST
- INITIATION AND PROPAGATION OF DAMAGE DURING DROP EVAPORATION TEST (en)
|
skos:notation
| - RIV/25794787:_____/09:#0000316!RIV11-MSM-25794787
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GA106/08/1789), Z(MSM2579478701)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/25794787:_____/09:#0000316
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Stainless steel; drop evaporation test; stress corrosion cracking; pitting (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/nazevZdroje
| - 17th International Corrosion Congress Proceedings
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Kalabisová, Eva
- Číhal, Vladimír
- Krhutová, Z.
- Lasek, S.
- Blahetová, M.
- Blaheta, R.
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
is http://linked.open...avai/riv/vysledek
of | |