| - The paper presents heterogeneous chemical composition of the steel slab, which was determined during short-time operation of continuous casting machine after flying tundish change. Before this exchange the steel A was cast (0.41 wt.% C and 0.95 wt.% Cr), shortly after the exchange continuous casting of the steel B (0.17 wt.% C and 0.70 wt.% Cr) started. After 20 minutes the continuous casting machine automatically stopped, because in the straightening zone, between the 7th and the 8th segment a breakout had occurred. Part of the slab was taken from the place of breakout for more precise determination of the position of breakout. It served also for taking the test samples for analysis of local chemical composition. It was expected that basic information on chemical heterogeneity of both steels A and B will be obtained, as well as information on exchange of mass between these two steels, which occurred some 20 minutes before stopping of the continuous casting machine. The reason was that structural stat
- The paper presents heterogeneous chemical composition of the steel slab, which was determined during short-time operation of continuous casting machine after flying tundish change. Before this exchange the steel A was cast (0.41 wt.% C and 0.95 wt.% Cr), shortly after the exchange continuous casting of the steel B (0.17 wt.% C and 0.70 wt.% Cr) started. After 20 minutes the continuous casting machine automatically stopped, because in the straightening zone, between the 7th and the 8th segment a breakout had occurred. Part of the slab was taken from the place of breakout for more precise determination of the position of breakout. It served also for taking the test samples for analysis of local chemical composition. It was expected that basic information on chemical heterogeneity of both steels A and B will be obtained, as well as information on exchange of mass between these two steels, which occurred some 20 minutes before stopping of the continuous casting machine. The reason was that structural stat (en)
|
Title
| - Heterogeneity of Continuously Cast Steel Slab Shortly Before Breakout
- Heterogeneity of Continuously Cast Steel Slab Shortly Before Breakout (en)
|
skos:prefLabel
| - Heterogeneity of Continuously Cast Steel Slab Shortly Before Breakout
- Heterogeneity of Continuously Cast Steel Slab Shortly Before Breakout (en)
|
skos:notation
| - RIV/00216305:26210/12:PU100094!RIV13-GA0-26210___
|
http://linked.open...avai/predkladatel
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26210/12:PU100094
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - concast slab, chemical composition, heterogeneity, breakout (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - METAL 2012 Conference proceedingd (CD-ROM)
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Dobrovská, Jana
- Kavička, František
- Sekanina, Bohumil
- Stránský, Karel
- Štětina, Josef
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |
is http://linked.open...avai/riv/vysledek
of | |