| - Experimental results of low-cycle fatigue loading of cylindrical specimens made of the cast nickel-based superalloy, Inconel 713LC, that were prepared with and without the diffusion aluminide coating are presented in the paper. Specimens were subjected to symmetrical bending and torsion loadings with the sine shape of the loading cycle of frequency f = 30 Hz under the load-control regime. Experiments were carried out at room temperature in the laboratory air environment by means of the testing stand MZGS-200 of the polish provenance up to a final rupture. In the case of bending loading, the diffusion coating leads to a decrease of the fatigue life. Conversely, the presence of the coating improves the fatigue performance in the case of the torsional loading. Fracture surfaces of selected specimens were observed in the scanning electron microscope. Fractographical analysis revealed that the different bending and torsion fatigue behaviour was mainly caused by different initiation mechanisms. An accelerat
- Experimental results of low-cycle fatigue loading of cylindrical specimens made of the cast nickel-based superalloy, Inconel 713LC, that were prepared with and without the diffusion aluminide coating are presented in the paper. Specimens were subjected to symmetrical bending and torsion loadings with the sine shape of the loading cycle of frequency f = 30 Hz under the load-control regime. Experiments were carried out at room temperature in the laboratory air environment by means of the testing stand MZGS-200 of the polish provenance up to a final rupture. In the case of bending loading, the diffusion coating leads to a decrease of the fatigue life. Conversely, the presence of the coating improves the fatigue performance in the case of the torsional loading. Fracture surfaces of selected specimens were observed in the scanning electron microscope. Fractographical analysis revealed that the different bending and torsion fatigue behaviour was mainly caused by different initiation mechanisms. An accelerat (en)
|
Title
| - Bending and Torsion Fatigue of Inconel 713LC with and withouth Diffusion Coating
- Bending and Torsion Fatigue of Inconel 713LC with and withouth Diffusion Coating (en)
|
skos:prefLabel
| - Bending and Torsion Fatigue of Inconel 713LC with and withouth Diffusion Coating
- Bending and Torsion Fatigue of Inconel 713LC with and withouth Diffusion Coating (en)
|
skos:notation
| - RIV/00216305:26210/11:PU96857!RIV13-MPO-26210___
|
http://linked.open...avai/predkladatel
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26210/11:PU96857
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - fatigue, bending, torsion, Inconel 713LC, diffusion coating (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - METAL 2011 Conference Proceedings
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Bonaventurová, Kateřina
- Pokluda, Jaroslav
- Slámečka, Karel
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |
is http://linked.open...avai/riv/vysledek
of | |