| - The paper presents results of the fractographical analysis of fish-eye cracks that were formed in plasmanitrided steel specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading combinations. Due to higher strength and compressive residual stresses introduced by plasma nitriding procedure, the subsurface fish-eye cracks were initiated inside the specimen bulk as a dominant failure mechanism. The geometrical characteristics of the fish-eye cracks (the radial asymmetry, the average size and the elliptical coefficient) were studied in the relation to the fish-eye crack location, the loading regime and the fatigue life. Both the ompressive residual stresses and the bending-torsion loading gradients were taken into account when discussing the results. Besides the well known fact that the nitrided surface layer reduces the crack growth rate, the study revealed that the average size of the fish-eye crack increases with both the distance from the free surface and th
- The paper presents results of the fractographical analysis of fish-eye cracks that were formed in plasmanitrided steel specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading combinations. Due to higher strength and compressive residual stresses introduced by plasma nitriding procedure, the subsurface fish-eye cracks were initiated inside the specimen bulk as a dominant failure mechanism. The geometrical characteristics of the fish-eye cracks (the radial asymmetry, the average size and the elliptical coefficient) were studied in the relation to the fish-eye crack location, the loading regime and the fatigue life. Both the ompressive residual stresses and the bending-torsion loading gradients were taken into account when discussing the results. Besides the well known fact that the nitrided surface layer reduces the crack growth rate, the study revealed that the average size of the fish-eye crack increases with both the distance from the free surface and th (en)
|
Title
| - Quantitative fractography of fish-eye crack formation under bending-torsion fatigue
- Quantitative fractography of fish-eye crack formation under bending-torsion fatigue (en)
|
skos:prefLabel
| - Quantitative fractography of fish-eye crack formation under bending-torsion fatigue
- Quantitative fractography of fish-eye crack formation under bending-torsion fatigue (en)
|
skos:notation
| - RIV/00216305:26210/10:PU85475!RIV10-MSM-26210___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GP106/08/P366), Z(MSM0021630518)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26210/10:PU85475
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Quantitative fractography, Fish-eye cracks, Bending-torsion fatigue, Plasma nitriding, Residual stress (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - GB - Spojené království Velké Británie a Severního Irska
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| - INTERNATIONAL JOURNAL OF FATIGUE
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Dvořák, Ivan
- Kianicová, Marta
- Pokluda, Jaroslav
- Slámečka, Karel
- Major, Štěpán
|
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://localhost/t...ganizacniJednotka
| |
is http://linked.open...avai/riv/vysledek
of | |