The alloys based on intermetallic compounds of iron and aluminium owing to their excellent resistance to oxidation and sulfidation are attractive for many high temperature applications. Therefore, their creep resistance, that is unfortunately relatively low, is very important. Improvements in this direction can be obtained through precipitation of second phase particles in basic Fe3Al matrix after addition of elements with a limited solubility. Within the project, the additions of carbide-forming elements will be studied together with the additions of carbon. The strengthening can then be achieved either by intermetallic phases, by the respective carbides or by their combination. (en)
Slitiny na bázi intermetalických sloučenin železa a hliníku jsou díky vynikající resistenci vůči oxidaci a sulfidaci perspektivní pro řadu vysokoteplotních aplikací. Mimořádnou důležitost má tedy jejich odolnost vůči tečení, která je však poměrně nízká. Zlepšení je možno dosáhnout pomocí částic sekundární fáze precipitujících v základní matrici Fe3Al po přidání prvků s omezenou rozpustností. V rámci projektu budou studovány přídavky karbidotvorných prvků spolu s přídavkem uhlíku, tak aby se dosáhlo zpevnění buď intermetalickými fázemi, nebo příslušnými karbidy nebo jejich kombinací.