| - The aim of the project is (i) to obtain the diffusion coefficients of hydrogen in Mg, Mg-xNi and Mg-xNi-yX alloys with the third element X that shows no significant tendency to hydride formation and (ii) to measure the hydrogen desorption spectras of modified (Mg-xNi-yX)-H alloys by DSC. The alloys will be prepared by ball-milling and following pressure compacting and by ball-milling followed by induction melting. Average Ni concentration will be x = 10, 23.5 (eutectic), 40, 54.5 (Mg2Ni) and 60 wt.%. Alloying elements X will be chosen from group II.-IV. (X: Zn, Ga, In, Si, Ge and Sn) and their concentration y will be in units of weight percent. Characteristics of the samples will be checked by electron microanalysis using SEM/EDAX and by DSC. Experimental temperatures will span from the room temperature up to the solidus. Diffusion coefficients will be obtained by tenzimetric method: The samples will be hydrogenised by gaseous hydrogen in a furnace. Diffusion coefficients will be calculated (en)
- Cílem projektu je (i) naměřit koeficienty difúze vodíku v Mg, ve slitinách Mg-xNi, a ve slitinách Mg-xNi-yX modifikovaných třetím elementem X který nevykazuje výraznou tendenci k tvorbě hydridů a (ii) změřit desorpční spektrum modifikovaných slitin (Mg-xNi-yX)-H metodou DSC. Slitiny budou připraveny jednak metodou mechanického legování v kulovém mlýnu a zkompaktováním mletého prášku a jednak mletím a následným přetavením. Průměrná koncentrace Ni bude x = 10; 23,5 (eutekticé složení); 40; 54,5 (Mg2Ni) a 60 váh. %. Legovací prvky X budou vybrány z grup II. - IV. (X = Zn, Ga, In, Si, Ge a Sn) a jejich koncentrace bude v jednotkách váh. %. Vzorky budou studovány pomocí SEM/EDAX a DSC. Experimentální teploty budou pokrývat oblast od pokojové teploty po solidus. Difúzní koeficienty budou měřeny tenzimetrickou metodou: Vzorky budou nasyceny vodíkem v peci z plynné fáze. Koeficienty difúze pak budou vypočteny ze záznamu závislosti tlaku desorbovaného vodíku na čase.
|
Title
| - Diffusion of hydrogen in alloys Mg-Ni modified by chosen elements that suppress the stability of hydrides (en)
- Difúze vodíku ve slitinách Mg-Ni modifikovaných vybranými prvky snižujícími stabilitu hydridů
|
skos:notation
| |
http://linked.open...avai/cep/aktivita
| |
http://linked.open...kovaStatniPodpora
| |
http://linked.open...ep/celkoveNaklady
| |
http://linked.open...datumDodatniDoRIV
| |
http://linked.open...i/cep/druhSouteze
| |
http://linked.open...ep/duvernostUdaju
| |
http://linked.open.../cep/fazeProjektu
| |
http://linked.open...ai/cep/hlavniObor
| |
http://linked.open...hodnoceniProjektu
| |
http://linked.open...vai/cep/kategorie
| |
http://linked.open.../cep/klicovaSlova
| - hydrogen; magnesium alloys; hydrogen storage; hydrides (en)
|
http://linked.open...ep/partnetrHlavni
| |
http://linked.open...inujicichPrijemcu
| |
http://linked.open...cep/pocetPrijemcu
| |
http://linked.open...ocetSpoluPrijemcu
| |
http://linked.open.../pocetVysledkuRIV
| |
http://linked.open...enychVysledkuVRIV
| |
http://linked.open...lneniVMinulemRoce
| |
http://linked.open.../prideleniPodpory
| |
http://linked.open...iciPoslednihoRoku
| |
http://linked.open...atUdajeProjZameru
| |
http://linked.open.../vavai/cep/soutez
| |
http://linked.open...usZobrazovaneFaze
| |
http://linked.open...ai/cep/typPojektu
| |
http://linked.open...ep/ukonceniReseni
| |
http://linked.open.../cep/vedlejsiObor
| |
http://linked.open...ep/zahajeniReseni
| |
http://linked.open...jektu+dodavatelem
| - . (en)
- V rámci projektu byly studovány charakteristiky slitin na bázi Mg-Ni určených pro skladování vodíku jako paliva pro výrobu energie. Cílem bylo jednak dosáhnout hlubšího porozumění zákonitostí, které určují rychlost desorpce vodíku ze slitiny a jednak nale (cs)
|
http://linked.open...tniCyklusProjektu
| |
http://linked.open.../cep/klicoveSlovo
| - hydrogen
- hydrogen storage
- magnesium alloys
|
is http://linked.open...vavai/riv/projekt
of | |
is http://linked.open...vavai/cep/projekt
of | |