| - Proposed project is devoted to sulphide stress cracking (SSC) of modem structural steels, i.e. micro alloy steels with a different yield strength, duplex steel containing austenite and ferrite and weldable supermartensitic steel with a low carbon and sulphur content. The main objective of the project is to prove that a common approach to determine steel resistance to SSC based on the steel hardness is quite insufficient and may be even dangerous. All parameters that determine steel resistance to SSC or more generally to hydrogen embrittlement have to be taken into account. An attention will be also paid to the choice of the method to test SSC resistance. Tests performed on specimens loaded below the yield strength will be compared with slow strain rate tensile tests (SSRTT) during which specimens are loaded to the failure. The material response may be different because during SSRTT interaction hydrogen - plastic deformation can occur and thus change crack initiation sites as well as the crack (en)
- Navrhovaný projekt je věnován sulfidickému praskání pod napětím (SSC) moderních konstrukčních ocelí, a to mikrolegovaných ocelí s rozdílnou mezí kluzu, dále duplexní austeniticko-feritické oceli a svařitelné supermartenzitické oceli s nízkým obsahem uhlíku a síry. Hlavním smyslem projektu je prokázat, že obvyklý přístup při posuzování odolnosti ocelí vůči SSC založený na tvrdosti je zcela nedostatečný a může být dokonce nebezpečný. V úvahu je třeba vzít všechny parametry, které ovlivňují odolnost ocelí vůči SSC, resp. obecněji vůči vodíkové křehkosti. Pozornost bude věnována i výběru zkušební metody pro určení odolnosti ocelí vůči SSC. Budou srovnány testy, při nichž je materiál zatížen pod mezí kluzu, s tahovou zkouškou za nízké rychlosti deformace, kdy jsou vzorky zatěžovány až do lomu. Odezva materiálu může být jiná, protože při druhém typu zkoušek se může výrazně uplatnit interakce vodík - plastická deformace, což může změnit iniciační místa vzniku trhlin i mechanizmus jejich šíření.
|
| Title
| - Sulphide stress cracking of modern structural steels (en)
- Sulfidické praskání pod napětím moderních konstrukčních ocelí
|
| skos:notation
| |
| http://linked.open...avai/cep/aktivita
| |
| http://linked.open...kovaStatniPodpora
| |
| http://linked.open...ep/celkoveNaklady
| |
| http://linked.open...datumDodatniDoRIV
| |
| http://linked.open...i/cep/druhSouteze
| |
| http://linked.open...ep/duvernostUdaju
| |
| http://linked.open.../cep/fazeProjektu
| |
| http://linked.open...ai/cep/hlavniObor
| |
| http://linked.open...hodnoceniProjektu
| |
| http://linked.open...vai/cep/kategorie
| |
| http://linked.open.../cep/klicovaSlova
| |
| http://linked.open...ep/partnetrHlavni
| |
| http://linked.open...inujicichPrijemcu
| |
| http://linked.open...cep/pocetPrijemcu
| |
| http://linked.open...ocetSpoluPrijemcu
| |
| http://linked.open.../pocetVysledkuRIV
| |
| http://linked.open...enychVysledkuVRIV
| |
| http://linked.open...okUkonceniPodpory
| |
| http://linked.open...okZahajeniPodpory
| |
| http://linked.open...iciPoslednihoRoku
| |
| http://linked.open...atUdajeProjZameru
| |
| http://linked.open.../vavai/cep/soutez
| |
| http://linked.open...usZobrazovaneFaze
| |
| http://linked.open...ai/cep/typPojektu
| |
| http://linked.open.../cep/vedlejsiObor
| |
| http://linked.open...jektu+dodavatelem
| - The grant project was devoted to the role of microstructure in the process of important degradation mechanism in hydrogen sulphide containing environments - sulphide stress cracking (SSC). The role of microstructure was studied at three different kinds o (en)
- Grant byl věnován roli mikrostruktury v případě závažného mechanismu degradace ocelí v prostředí sirovodíku - sulfidickému praskání pod napěním (SSC). Vliv mikrostruktury byl studován u tří rozdílných typů konstrukčních ocelí používaných v ropném průmysl (cs)
|
| http://linked.open...tniCyklusProjektu
| |
| is http://linked.open...vavai/riv/projekt
of | |
| is http://linked.open...vavai/cep/projekt
of | |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)