| - The project comprises an improving of computational techniques for assesment of residual life of bodies with fatigue cracks with respect to the influence of following factors: geometry of a body, corner stress singularity, roughness of fracture surfaces,bi-material interface, in-plane and out-of-plane constraint and local low-cycle plastic and fracture properties of material. Input data for 2D and 3D FE models will be obtained from fatigue crack experiments in threshold area and low-cycle fatigue experiments. The distribution of the T-stress along the crack front and stress singularity change near the free surface and bi-material interface influence on crack behavior will be studied using FE computations. The results will be applied to crack front shape and rate prediction in bodies with complicated geometry and material composition. Nonlinear elastic-plastic FE models will be used for fatigue crack growth prediction based on local fracture criteria for microscopic low-cycle fatigue. The (en)
- Projekt je zaměřen na zpřesnění výpočtových postupů pro odhad zbytkové životnosti těles s únavovými trhlinami, respektující zejména vliv geometrie tělesa, rohové singularity napětí, drsnosti lomových ploch, materiálového rozhraní, stísnění deformace a lokálních nízkocyklových plastických a lomových vlastností materiálu. Vstupní údaje pro 2D a 3D MKP modely budou získány experimentálním sledováním růstu únavových trhlin v prahové oblasti a nízkocyklovými únavovými zkouškami. MKP výpočty budou použity hlavně na studium rozložení T-napětí na čele trhliny, změny singularity u volného povrchu a vlivu materiálového rozhraní na chování trhliny. Výsledky budou aplikovány při predikci tvaru a rychlosti čela únavové trhliny u těles s komplikovanou geometrií a materiálovou stavbou. Elastoplastické MKP simulace únavových trhlin budou zaměřeny na možnosti predikce rychlosti jejich šíření pomocí lokálních lomových kriterií pro mikroskopickou nízkocyklovou únavu na jejich čele. Testováno bude zejména kriterium
|
Title
| - Innovative techniques for assessment of residual life of bodies with fatigue cracks (en)
- Inovační postupy pro odhad zbytkové životnosti těles s únavovými trhlinami
|
skos:notation
| |
http://linked.open...avai/cep/aktivita
| |
http://linked.open...kovaStatniPodpora
| |
http://linked.open...ep/celkoveNaklady
| |
http://linked.open...datumDodatniDoRIV
| |
http://linked.open...i/cep/druhSouteze
| |
http://linked.open...ep/duvernostUdaju
| |
http://linked.open.../cep/fazeProjektu
| |
http://linked.open...ai/cep/hlavniObor
| |
http://linked.open...hodnoceniProjektu
| |
http://linked.open...vai/cep/kategorie
| |
http://linked.open.../cep/klicovaSlova
| - fatigue; fatigue crack growth; damage mechanics; fracture mechanics; T-stress; finite element method (en)
|
http://linked.open...ep/partnetrHlavni
| |
http://linked.open...inujicichPrijemcu
| |
http://linked.open...cep/pocetPrijemcu
| |
http://linked.open...ocetSpoluPrijemcu
| |
http://linked.open.../pocetVysledkuRIV
| |
http://linked.open...enychVysledkuVRIV
| |
http://linked.open...lneniVMinulemRoce
| |
http://linked.open.../prideleniPodpory
| |
http://linked.open...iciPoslednihoRoku
| |
http://linked.open...atUdajeProjZameru
| |
http://linked.open.../vavai/cep/soutez
| |
http://linked.open...usZobrazovaneFaze
| |
http://linked.open...ai/cep/typPojektu
| |
http://linked.open...ep/ukonceniReseni
| |
http://linked.open...ep/zahajeniReseni
| |
http://linked.open...jektu+dodavatelem
| - . (en)
- Jedná se o vynikající projekt řešený kvalitním řešitelským kolektivem. Přestože se jedná o %22pouze%22 dvouletý projekt přináší výsledky řešení řadu nových poznatků o mechanismu a rychlosti růstu únavových trhlin, které je možno uplatnit při predikci zbytkové (cs)
|
http://linked.open...tniCyklusProjektu
| |
http://linked.open.../cep/klicoveSlovo
| - fatigue
- T-stress
- damage mechanics
- fatigue crack growth
- fracture mechanics
|
is http://linked.open...vavai/riv/projekt
of | |
is http://linked.open...vavai/cep/projekt
of | |