About: Stress Corrosion Cracking of Austenitic Stainless Steels in Simulated Nuclear Reactor Conditions     Goto   Sponge   NotDistinct   Permalink

An Entity of Type : http://linked.opendata.cz/ontology/domain/vavai/Vysledek, within Data Space : linked.opendata.cz associated with source document(s)

AttributesValues
rdf:type
Description
  • Stress corrosion cracking (SCC) susceptibility of selected austenitic stainless steels was investigated within the SAFELIFE and HPLWR-2 projects. The aim was to identify and describe the specific failure mechanisms in simulated reactor conditions, i.e., a combination of slow strain rate and high temperature in different environments. Slow J-R and standard SCC tests of AISI 304L stainless steel with different degree of cold working were carried out under BWR condition. Slow strain-rate tensile (SSRT) tests of 316L stainless steel were carried out in ultra-pure demineralized supercritical water (SCW) solution. Tested specimens were subjected to fractographic analysis in order to characterize the failure mechanisms. The specimens failed due to a combination of transgranular SCC and transgranular ductile fracture. The ratio of SCC and ductile fracture was affected by the parameters of tests, in particular by temperature, pressure, oxygen content and strain rate.
  • Stress corrosion cracking (SCC) susceptibility of selected austenitic stainless steels was investigated within the SAFELIFE and HPLWR-2 projects. The aim was to identify and describe the specific failure mechanisms in simulated reactor conditions, i.e., a combination of slow strain rate and high temperature in different environments. Slow J-R and standard SCC tests of AISI 304L stainless steel with different degree of cold working were carried out under BWR condition. Slow strain-rate tensile (SSRT) tests of 316L stainless steel were carried out in ultra-pure demineralized supercritical water (SCW) solution. Tested specimens were subjected to fractographic analysis in order to characterize the failure mechanisms. The specimens failed due to a combination of transgranular SCC and transgranular ductile fracture. The ratio of SCC and ductile fracture was affected by the parameters of tests, in particular by temperature, pressure, oxygen content and strain rate. (en)
Title
  • Stress Corrosion Cracking of Austenitic Stainless Steels in Simulated Nuclear Reactor Conditions
  • Stress Corrosion Cracking of Austenitic Stainless Steels in Simulated Nuclear Reactor Conditions (en)
skos:prefLabel
  • Stress Corrosion Cracking of Austenitic Stainless Steels in Simulated Nuclear Reactor Conditions
  • Stress Corrosion Cracking of Austenitic Stainless Steels in Simulated Nuclear Reactor Conditions (en)
skos:notation
  • RIV/68407700:21340/10:00173841!RIV11-MSM-21340___
http://linked.open...avai/riv/aktivita
http://linked.open...avai/riv/aktivity
  • Z(MSM6840770021)
http://linked.open...vai/riv/dodaniDat
http://linked.open...aciTvurceVysledku
http://linked.open.../riv/druhVysledku
http://linked.open...iv/duvernostUdaju
http://linked.open...titaPredkladatele
http://linked.open...dnocenehoVysledku
  • 290332
http://linked.open...ai/riv/idVysledku
  • RIV/68407700:21340/10:00173841
http://linked.open...riv/jazykVysledku
http://linked.open.../riv/klicovaSlova
  • stress corrosion cracking; fractography; austenitic stainless steels (en)
http://linked.open.../riv/klicoveSlovo
http://linked.open...ontrolniKodProRIV
  • [D9A347DE5CFB]
http://linked.open...v/mistoKonaniAkce
  • Ostrava
http://linked.open...i/riv/mistoVydani
  • Ostrava
http://linked.open...i/riv/nazevZdroje
  • New Methods of Damage and Failure Analysis of Structural Parts
http://linked.open...in/vavai/riv/obor
http://linked.open...ichTvurcuVysledku
http://linked.open...cetTvurcuVysledku
http://linked.open...UplatneniVysledku
http://linked.open...iv/tvurceVysledku
  • Haušild, Petr
  • Novotný, R.
  • Siegl, Jan
  • Nedbal, Ivan
http://linked.open...vavai/riv/typAkce
http://linked.open.../riv/zahajeniAkce
http://linked.open...n/vavai/riv/zamer
number of pages
http://purl.org/ne...btex#hasPublisher
  • Vysoká škola báňská - Technická univerzita Ostrava
https://schema.org/isbn
  • 978-80-248-2265-5
http://localhost/t...ganizacniJednotka
  • 21340
Faceted Search & Find service v1.16.118 as of Jun 21 2024


Alternative Linked Data Documents: ODE     Content Formats:   [cxml] [csv]     RDF   [text] [turtle] [ld+json] [rdf+json] [rdf+xml]     ODATA   [atom+xml] [odata+json]     Microdata   [microdata+json] [html]    About   
This material is Open Knowledge   W3C Semantic Web Technology [RDF Data] Valid XHTML + RDFa
OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 58 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software