| - Mechanical property degradation of fuel cladding is caused by steam exposure during normal service operation of nuclear reactor and especially during LOCA accident. Resulting damage of fuel cladding may directly lead to fatal radioactivity leakage. Thus the degradation processes that may take place if fuel claddings after exposure in the harsh nuclear reactor environment are extensively studied. The paper summarizes the influence of exposure in 1000°C steam and subsequent rapid cooling on fracture behaviour of two different Zr alloys commonly used for fuel claddings. The fractographic analysis describes microfractographic features of cladding tube failure and uncovers phase transformations taking place in different areas of the tube wall. The results of fractographic analysis correlate well with hydrogen contents in the cladding material and results of tensile test. (en)
- Degradace mechanických vlastností povlakových trubek palivových článků v důsledku expozice v běžných provozních nebo havarijních podmínkách jaderných reaktorů, může vést k porušení integrity článků a úniku radioaktivity. Z uvedených důvodů je stále větší pozornost věnována výzkumu degradačních procesů, ke kterým by v materiálu povlakových trubek mohlo dojít za různých exploatačních podmínek. V příspěvku jsou shrnuty hlavní výsledky experimentů, zaměřených na hodnocení vlivu expozice v páře o teplotě 1 000°C a následného rychlého ochlazení na lomové chování dvou Zr-slitin, používaných pro výrobu povlakových trubek. Při fraktografické analýze byly popsány mikrofraktografické znaky porušování sledovaných trubek. Získané výsledky jsou významným přínosem při rozboru a interpretaci výsledků získaných různými experimentálními postupy.
- Degradace mechanických vlastností povlakových trubek palivových článků v důsledku expozice v běžných provozních nebo havarijních podmínkách jaderných reaktorů, může vést k porušení integrity článků a úniku radioaktivity. Z uvedených důvodů je stále větší pozornost věnována výzkumu degradačních procesů, ke kterým by v materiálu povlakových trubek mohlo dojít za různých exploatačních podmínek. V příspěvku jsou shrnuty hlavní výsledky experimentů, zaměřených na hodnocení vlivu expozice v páře o teplotě 1 000°C a následného rychlého ochlazení na lomové chování dvou Zr-slitin, používaných pro výrobu povlakových trubek. Při fraktografické analýze byly popsány mikrofraktografické znaky porušování sledovaných trubek. Získané výsledky jsou významným přínosem při rozboru a interpretaci výsledků získaných různými experimentálními postupy. (cs)
|
| Title
| - Porušování povlakových trubek ze Zr-slitin při simulaci havárie LOCA
- Porušování povlakových trubek ze Zr-slitin při simulaci havárie LOCA (cs)
- Failure of Zr-Alloy Cladding of Fuel Rods during LOCA Accident Simulation (en)
|
| skos:prefLabel
| - Porušování povlakových trubek ze Zr-slitin při simulaci havárie LOCA
- Porušování povlakových trubek ze Zr-slitin při simulaci havárie LOCA (cs)
- Failure of Zr-Alloy Cladding of Fuel Rods during LOCA Accident Simulation (en)
|
| skos:notation
| - RIV/68407700:21340/06:04121765!RIV07-MSM-21340___
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21340/06:04121765
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Zr-alloys; cladding; corrosion layer; ductility; embrittlement; fracture micromorphology; oxygen stabilized alfa; prior beta; steam exposure (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...v/mistoKonaniAkce
| |
| http://linked.open...i/riv/mistoVydani
| |
| http://linked.open...i/riv/nazevZdroje
| |
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...iv/tvurceVysledku
| - Kovářík, Ondřej
- Siegl, Jan
- Adámek, Jan
- Vrtílková, V.
|
| http://linked.open...vavai/riv/typAkce
| |
| http://linked.open.../riv/zahajeniAkce
| |
| http://linked.open...n/vavai/riv/zamer
| |
| number of pages
| |
| http://purl.org/ne...btex#hasPublisher
| - Ústav materiálového výskumu SAV
|
| https://schema.org/isbn
| |
| http://localhost/t...ganizacniJednotka
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)