| - A study of fatigue behaviour an Fe-28Al-3Cr-Ce (at%) based alloy was carried out on compact tension (CT) specimens 5 mm in thickness. The specimens were loaded in tension at 20, 300 and 500°C with 10 Hz frequency and R in the range from 0.05 to 0.1.The fatigue crack growth rate was measured by the potential method. The number of cycles to failure decreases rapidly with temperature. The fatigue crack propagation rate at RT and elevated temperatures is different. The slope of v(DK) curves is much steeper at RT, while it remains almost the same at 300 and 500°C. The fatigue crack growth rate at 500°C is nearly two orders higher than at 300°C. Fractographic analysis showed that at room temperature fatigue crack growth is controlled by several mechanisms. The main failure mechanism is transgranular cleavage, crack growth by the brittle or ductile striation mechanism is localized only in several areas along the crack front.
- A study of fatigue behaviour an Fe-28Al-3Cr-Ce (at%) based alloy was carried out on compact tension (CT) specimens 5 mm in thickness. The specimens were loaded in tension at 20, 300 and 500°C with 10 Hz frequency and R in the range from 0.05 to 0.1.The fatigue crack growth rate was measured by the potential method. The number of cycles to failure decreases rapidly with temperature. The fatigue crack propagation rate at RT and elevated temperatures is different. The slope of v(DK) curves is much steeper at RT, while it remains almost the same at 300 and 500°C. The fatigue crack growth rate at 500°C is nearly two orders higher than at 300°C. Fractographic analysis showed that at room temperature fatigue crack growth is controlled by several mechanisms. The main failure mechanism is transgranular cleavage, crack growth by the brittle or ductile striation mechanism is localized only in several areas along the crack front. (en)
- Únavové chování slitiny Fe-28Al-3Cr-Ce bylo studováno na CT tělesech tloušťky 5 mm. Vzorky byly zatěžovány v tahu při teplotě 20, 300 a 500°C při frekvenci 10 Hz a parametru asymetrie cyklu R v rozmezí 0.05 až 0.1. Rychlost šíření únavové trhliny byla sledována pomocí potenciálové metody. Počet cyklů do porušení s teplotou výrazně klesá. Únavová trhlina se při pokojové teplotě a při zvýšených teplotách šíří odlišně. Směrnice křivek v(DK) je strmější při pokojové teplotě, zatímco při 300 a 500°C zůstává v podstatě stejná. Rychlost šíření únavové trhliny při 500°C je téměř o dva řády vyšší než při teplotě 300°C. Fraktografická analýza ukázala, že únavová trhlina se při pokjové teplotě šíří několika mechanismy. Hlavní mechanismus je transkrystalické štěpení, šíření trhliny mechanismem křehkých či tvárných striací je lokalizováno pouze v několika oblstech podél čela trhliny. (cs)
|
| Title
| - Behaviour of an Fe-28Al-3Cr-Ce Alloy under Cyclic Loading
- Behaviour of an Fe-28Al-3Cr-Ce Alloy under Cyclic Loading (en)
- Únavové chování slitiny Fe-28Al-3Cr-Ce při cyklickém zatěžování (cs)
|
| skos:prefLabel
| - Behaviour of an Fe-28Al-3Cr-Ce Alloy under Cyclic Loading
- Behaviour of an Fe-28Al-3Cr-Ce Alloy under Cyclic Loading (en)
- Únavové chování slitiny Fe-28Al-3Cr-Ce při cyklickém zatěžování (cs)
|
| skos:notation
| - RIV/68407700:21340/04:04099771!RIV/2005/GA0/213405/N
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...iv/cisloPeriodika
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21340/04:04099771
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Fe3Al based intermetallics; crack propagation; fatigue; fractography; scanning electron microscopy (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...odStatuVydavatele
| |
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...i/riv/nazevZdroje
| - Journal of Alloys and Compounds
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...vavai/riv/projekt
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...v/svazekPeriodika
| |
| http://linked.open...iv/tvurceVysledku
| - Siegl, Jan
- Karlík, Miroslav
- Nedbal, Ivan
- Prahl, Jakub
|
| issn
| |
| number of pages
| |
| http://localhost/t...ganizacniJednotka
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)