| - CrCN coatings were prepared by cathode arc evaporation technology using constant N2 flow and variable C2H2 flow. The coatings with a thickness of 3-4 μm were deposited on hardened steel substrates and high-temperature resistant alloy. The carbon content varied from 0 at.% (i.e. CrN) up to 31 at.%. The standard coating characterization included the nano-hardness, adhesion, chemical composition and structure (including hot X-ray diffraction). Wear testing was done using a high temperature tribometer (pin-on-disc); the maximum testing temperature was 700 oC. The coatings with carbon content 12-31 at.% showed almost identical tribological behaviour up to 700 oC.
- CrCN coatings were prepared by cathode arc evaporation technology using constant N2 flow and variable C2H2 flow. The coatings with a thickness of 3-4 μm were deposited on hardened steel substrates and high-temperature resistant alloy. The carbon content varied from 0 at.% (i.e. CrN) up to 31 at.%. The standard coating characterization included the nano-hardness, adhesion, chemical composition and structure (including hot X-ray diffraction). Wear testing was done using a high temperature tribometer (pin-on-disc); the maximum testing temperature was 700 oC. The coatings with carbon content 12-31 at.% showed almost identical tribological behaviour up to 700 oC. (en)
|
Title
| - Effects of carbon content on the high temperature friction and wear of chromium carbonitride coatings
- Effects of carbon content on the high temperature friction and wear of chromium carbonitride coatings (en)
|
skos:prefLabel
| - Effects of carbon content on the high temperature friction and wear of chromium carbonitride coatings
- Effects of carbon content on the high temperature friction and wear of chromium carbonitride coatings (en)
|
skos:notation
| - RIV/68407700:21260/10:00168459!RIV11-MSM-21260___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(KJB201240701), Z(MSM6840770038)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21260/10:00168459
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - tribology; chromium nitride; carbonitride; high temperature (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Cavaleiro, A.
- Polcar, Tomáš
- Cvrček, Ladislav
- Vítů, Tomáš
- Vyskočil, J.
|
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://localhost/t...ganizacniJednotka
| |